Effects of Dentin Surface Treatments on the Fracture Toughness and Tensile Bond Strength of a Dentin-Composite Adhesive Interface

Abstract

It has been proposed that the fracture toughness test provides an appropriate method for assessing the fracture resistance of the dentin-composite interface. The plane-strain fracture toughness test was therefore applied to a dentin-composite interface, with use of a specific dentinal adhesive, so that the effects of various dentin surface treatments on dentin-bond integrity could be studied. Interfacial fracture toughness (K_IC) values were determined following 24 h and 180 days of specimen aging in distilled water at 37*C. Tensile bond strength (TBS) results following 24-hour aging were also obtained for comparison with the 24-hour K_IC results.

In general, the fracture resistance of the dentin-composite interface was highest when the dentin surface was conditioned with acid but not air-dried, intermediate when the dentin surface was conditioned with acid and subsequently air-dried, and lowest when the dentin was not conditioned with acid. The tensile bond strength results differed from the fracture toughness results in indicating differences in surface preparation effects and the type of interfacial failure observed.

Keywords

Bonding Dental Dental Materials Failure of Dental Materials Fractures.

References

Aquilino S. , Williams V. (1987). The effect of storage time on dentinal adhesive bond strengths (abstract). J Dent Res 66:292.

Baier R. (1992). Principles of adhesion. Oper Dent (Suppl 5):1-9.

Barkmeier W. , Suh B. , Cooley R. (1991). Shear bond strength to dentin and Ni-Cr-Be alloy with the All-bond Universal Adhesive System. J Esthet Dent 3:148-153.

Chan D. , Reinhardt J. , Boyer D. (1985). Composite resin compatibility and bond longevity of a dentin bonding agent. J Dent Res 64:1402-1404.

Chiba M. , Itoh K. , Wakumoto S. (1989). Effect of dentin cleansers on the bonding efficacy of dentin adhesive. Dent Mater J 8:76-85.

Erikson R. (1992). Surface interactions of dentin adhesive materials . Oper Dent (Suppl 5):81-94.

Gwinnett A. (1992). Moist versus dry dentin: its effect on shear bond strength. Am J Dent 5:127-129.

Gwinnett A. , Kanca III (1992a). Micromorphological relationship between resin and dentin in vivo and in vitro. Am J Dent 5:19-23.

Gwinnett A. , Kanca J. III (1992b). Micromorphology of the bonded dentin interface and its relationship to bond strength. Am J Dent 5:73-77.

10.

Gwinnett A. , Dickerson W. , Yu S. (1992). Dentin bond shear strength and microleakage for Syntac/Heliomolar: a comparison between the manufacturer's and total etch technique. J Esthet Dent 4:164-168.

11.

Hansen S. , Swift E. Jr (1992). Permeability effects of two dentin adhesive systems .JEsthet Dent 4:169-172.

12.

Kanca J. III (1991). Dental adhesion and the All-Bond System. J Esthet Dent 3:129-132.

13.

Kanca J. III (1992). Resin bonding to wet substrate. I. Bonding to dentin. Quint Int 23:39-41.

14.

Lino Carracho A. , Chappell R. , Glaros A. , Purk J. , Eick J. ( 1991). The effect of storage and thermocycling on the shear bond strength of three dentinal adhesives. Quint Int 22:745-752.

15.

Mitchem J. , Gronas D. (1991). Adhesion to dentin with and without smear layer under varying degress of wetness. J Prosthet Dent 66:619-622.

16.

Nakabayashi N. (1992). The hybrid layer: a resin-dentin composite. Proc Finn Dent Soc 88(Suppl 1):321-329.

17.

ilo G. , Olsson S. (1990). Tensile bond strength of dentin adhesives: a comparison of materials and methods. Dent Mater 6:138-144.

18.

Pashley D. (1991). The effects of acid etching on the pulpodentin complex. Oper Dent 17:229-242.

19.

Prati C. , Biagini G. , Nucci C. , Castaldini C. , Zucchini C. (1990). Effects of chemical pretreatments on dentin bonding . Am J Dent 3:199-206.

20.

Prati C. , Simpson M. , Mitchem J. , Tao L. , Pashley D. (1992). Relationship between bond strength and microleakage measured in the same class 1 restorations. Dent Mater 8:37-41.

21.

Rasmussen S. (1978). Fracture studies of adhesion. J Dent Res 57:11-20.

22.

Retief DH , O'Brien J. , Smith L. , Marchman J. (1988). In vitro investigation and evaluation of dentin bonding agents. Am J Dent 1:176-183.

23.

Retief DH , Mandras RS , Russell CM , Denys FR (1992). Phosphoric acid as a dentin etchant. Am J Dent 5:24-28.

24.

Ruse ND , Smith DC (1991). Adhesion to bovine dentin-surface characterization . J Dent Res 70:1002-1008.

25.

Shintani H. , Satou N. , Satou J. (1989). Clinical evaluation of two posterior composites retained with bonding agent. J Prosthet Dent 62:627-632.

26.

Sorensen J. , Dixit N. (1991). In vitro shear bond strength of dentin adhesives . Int J Prosth 4:117-125.

27.

Suh B. (1992). All-Bond-Fourth generation dentin bonding system . J Esthet Dent 3:139-147.

28.

Tam LE , Pilliar RM (1993). Fracture toughness of dentin/resincomposite adhesive interfaces. J Dent Res 72:953-959.

29.

Van Meerbeek B. , Inokoshi S. , Braem M. , Lambrechts P. , Vanherle G. (1992). Morphological aspects of the resin-dentin interdif fusion zone with different dentin adhesive systems. J Dent Res 71:1530-1540.

30.

Van Meerbeek B. , Willems G. , Celis JP , Roos JR , Braem M. , Lambrechts P. , et al. (1993). Assessment by nano-indentation of the hardness and elasticity of the resin-dentin bonding area. J Dent Res 72:1434-1442.

31.

Van Noort R. , Noroozi S. , Howard IC , Cardew GE (1989). A critique of bond strength measurements. J Dent 17:61-67.

32.

Van Noort R. , Cardew GE , Howard IC , Noroozi S. (1991). The effect of local interfacial geometry on the measurement of the tensile bond strength to dentin. J Dent Res 70:889-893.

33.

Wang T. , Nakabayashi N. (1991). Effect of 2-(methacryloxy)ethyl phenyl hydrogen phosphate on adhesion to dentin. J Dent Res 70:59-66.