A TEM Study of the Causes of Failure in the Chlorine-Hercosett® Shrink-Resist Process

Abstract

Examination by transmission electron microscopy of fibers drawn from two card slivers commercially treated by the chlorine-Hercosett® process showed the Hercosett film to be continuous over each fiber. One sliver had passed the Superwash test; almost all of the cuticular scales were flattened or sloping. Most of the fibers retained no steep scales, and none retained more than 20%. Previous work indicates that the modified scales would be much softer in water than unmodified scales. The Hercosett film on these fibers was at least 0.1 μm thick everywhere.

The other sliver had failed the Superwash test, half the fibers resembled those in the first sliver, but among the other half a high proportion of the scales (from 30- 70% on different fibers) remained steep (and, correspondingly, relatively hard). On half of these the film thickness was 0. 1 μm or greater; on the other half it was less than 0.05 μm either all over or on the remaining steep scale faces.

The character of these differences is such as to explain the failure of the process in the case of the second sliver. The difference in the scale shape indicates that the

failure resulted from non-uniformity of chlorination. The resin considerably pene trated the cuticle.

References

Anderson, C.A. , Katz, H.J. , Lipson, M. , and Wood, G.F. , Stereoscan Microscopy of Chlorine/Resin Treated Wool, Textile Res. J. 40, 29-34 (1970).

AWC Test Specification AWC/A43 for Care Claim Superwash. Australian Wool Corporation, Melbourne 1978.

Byrne, K. M., IWS Technical Centre, U.K., private communication, 1981.

Feldtman, H.D. , McPhee, J.R. , and Morgan, W.V. , Shrinkproofing Wool Tops, Textile Manuf. 93, 122-124 (1967).

García Dominguez, J. , Julia, M.R. , de la Maza, A. , Pujol, J.M. , and Sanchez, J. , A Method for Determining the Distribution of Cationic Shrink-Resist Resins on Wool. J. Soc. Dyers Colour. 92, 433-439 (1976).

Hine, R.J. and McPhee, J.R. , Light Microscopy of Polymer-Treated Wool, Textile Res. J. 34, 659-662 (1964).

Kershaw, A. , and Lewis, J. , The Role of Polymer Treatments in the Shrinkproofing of Wool, Textile Mon., No. 4, 40-44 (1976).

Lewis, J. , Superwash Wool, Part 2: Continuous Shrinkproofing Processes, Wool Sci. Rev., No. 55, 22-42 (1978).

Makinson, K.R. , and Lead, J.A. , The Nature and Function of the Resin in the Chlorine/Resin Shrinkproofing Treatment of Wool Tops, Textile Res. J. 43, 669-681 ( 1973).

10.

Makinson, K.R. , "Shrinkproofing of Wool." Marcel Dekker, N.Y., 1979. (a) p. 238, (b) pp. 202-5.

11.

Tester. D.H. . and Makinson, K.R. Transmission Electron Microscope Studies of the Permanganate/Salt Shrinkproofing Treatment of Wool, Textile Res. J. 52, 227-232 ( 1982).