Experimental studies were carried out to understand the impactor mass effects on glass–epoxy composites using an instrumented impact machine (DYNATUP 8250) under low-velocity test conditions. Repeated drop tests were carried out at pre-determined energy levels for selective mass height combinations. Number of drops to failure (Nf) was chosen as the damage criterion.
Analysis of test results clearly showed that, at low incident energies, heavier impactors caused more damage to the laminates as reflected by their lower number of drops to failure. This effect diminished gradually at relatively higher incident energies.
1. Cantwell, W.J. and Morton, J. (November 1989). Comparison of Low and High Velocity Impact Response of CFRP , Composites, 20(6): 549–551 .
2.
2. Suemasu, Hiroshi , Kerth, Steffan and Maier, Martin (1994). Indentation of Spherical Head Indentors on Transversely Isotropic Composite Plates , Journal of Composite Materials, 28(17): 1723–1739 .
3.
3. Qian, Y. , Swanson, S.R. , Nuismer, R.J. and Bucinell, R.B. (May 1990). An Experimental Study of Scaling Rules for Impact Damage in Fiber Composites , Journal of Composite Materials, 24: 559–570 .
4.
4. Sjoblom, Peter, O. , Hartness, Timothy. J. and Cordell, Tobey, M. (Jan 1988). On Low-velocity Impact Testing of Composite Materials , Journal of Composite Materials, 22: 30–52 .
5.
5. Choi, Hyung Yun , Downs, R.J. and Chang, Fu-Kuo (1991). A New Approach Towards Understanding Damage Mechanisms and Mechanics of Laminated Composites due to Low-velocity Impact: Part I – Experiments , Journal of Composite Materials, 25: 992–1011 .
6.
6. Chaturvedi, Shive, K. and Sierakowski, Robert L. (Mar 1985). Effects of Impactor Size on Impact Damage Growth and Residual Properties in an SMC-R50 Composite , Journal of Composite Materials, 19: 100–113 .
7.
7. Cantwell, W.J. and Morton, J. (1989). Geometrical Effects in the Low Velocity Impact Response of CFRP , Composite Structures, 12: 39–59 .
8.
8. Mittal, R.K. and Jafri, M.S. (1995). Influence of Fibre Content and Impactor Parameters on Transverse Impact Response of Uniaxially Reinforced Composite Plates , Composites, 26(12): 877–886 .
9.
9. Kumar, Prashant and Rai, Badri (1991). Impact Damage on Single Interface GFRP Laminates – An Experimental Study , Composite Structures, 18: 1–10 .
10.
10. Gros, Xavier E. (Mar 1996). Characterisation of Low Energy Impact Damage in Composites , Journal of Reinforced Plastics and Composites, 15: 267–282 .
11.
11. Yigit, A.S. and Christoforou, A.P. (1995). On the Impact Between a Rigid Sphere and a Thin Composite Laminate Supported by a Rigid Substrate , Composite Structures, 30: 169–177 .
12.
12. Gu, Z.L. and Sun, C.T. (1987). Prediction of Impact Region in SMC Composites , Composite Structures, 7: 179–190 .
13.
13. Dorey, G. , Sidey, G.R. and Hutchings, J. (Jan 1978). Impact Properties of Carbon Fibre/kevlar 49 Fibre Hybrid Composites , Composites, 9: 25–32 .
14.
14. Khan, Bijoysri , Rao, R.M.V.G.K. and Venkataraman, N. (Nov 1995). Low-velocity Impact Fatigue Studies on Glass Epoxy Composite Laminates with Varied Material and Test Parameters – Effect of Incident Energy and Fibre Volume Fraction , Journal of Reinforced Plastics and Composites, 14: 1150–1159 .