The Effect of Curing Conditions on the Properties of Silica Modified Glass Fiber Reinforced Epoxy Composite

Abstract

The effects of curing conditions on the mechanical properties of glass fiber reinforced epoxy composites under different fiber prestressing levels were quantitatively studied. The composite samples were prepared with silica particle modified continuous E-glass fibers, epoxy resin matrix, fiber prestressing and step curing processing. Room temperature cured and isothermal high temperature cured composite samples, with the same content and structure, were made to study the difference of three curing conditions on a quantitative level. Based on the test results of flexural, shear, and impact properties of the composite samples, it was found that the step curing procedure generates composite samples with up to 47% and 14% increased properties than room temperature cured and isothermal high temperature cured samples, respectively, when manufactured under the same fiber prestressing level. The possibility of generating an optimum residual stress within the samples during processing is proposed and discussed to explain the contribution of the step curing process to the composite properties.

Keywords

step curing room temperature curing isothermal high temperature curing flexural shear impact residual stress silica particle glass fiber epoxy modification prestressing

References

Sinclair, J. W. (1992). Effects of Cure Temperature on Epoxy Resin Properties , Journal of Adhesion, 38(3/4): 219-234 .

Wang, X. and Gillham, J. K. (1992). Analysis of Crosslinking in Amine-cured Epoxy Systems: The One-to-one Relationship between Tg and Conversion , Journal of Applied Polymer Science, 45(12): 2127-2143 .

Vakil, U. M. and Martin, G. C. (1992). Network Structure Characterization and Physical-mechanical Properties , Journal of Applied Polymer Science, 46(12): 2089-2099 .

Chang, S. (1992). Effect of Curing History on Ultimate Glass Transition Temperature and Network Structure of Crosslinking Polymers , Polymer, 33(22): 4768-4778 .

Lapique, F. and Redford, K. (2002). Curing Effects on Viscosity and Mechanical Properties of a Commercial Epox Resin Adhesive , International Journal of Adhesion and Adhesives, 22: 337-346 .

Huang, Y. and Young, R. J. (1995). Interfacial Behaviour in High Temperature Cured Carbon Fibre/Epoxy Resin Model Composite , Composites, 26: 541-550 .

Segovia, F. , Ferrer, C. , Salvador, M. D. and Amigo, V. (2001). Influence of Processing Variables on Mechanical Characteristics of Sunlight Aged Polyester-Glass Fibre Composites , Polymer Degradation and Stability, 71: 179-184 .

Segovia, F. , Salvador, M. D. , Amigo, V. and Vicente, A. (2003). Cure Effects on Post-Impact Tensile Characteristics of 2D Epoxy Composites , Journal of Materials Processing Technology, 143-144: 209-213 .

Kotani, M. , Inoue, T. , Kohyama, A. , Okamura, K. and Katoh, Y. (2002). Consolidation of Polymer-Derived SiC Matrix Composites: Processing and Microstructure , Composites Science and Technology, 62: 2179-2188 .

10.

Kam, T. Y. , Lai, F. M. and Sher, H. F. (1995). Optimal Parameters for Curing Graphite/Epoxy Composite Laminates , Journal of Materials Processing Technology, 48: 357-363 .

11.

Deb, S. and Sehmi, H. (2003). A Comparative Study of the Properties of Dental Resin Composites Polymerized with Plasma and Halogen Light , Dental Materials, 19: 517-522 .

12.

Motahhari, S. and Cameron, J. (1999). Fibre Prestressed Composites: Improvement of Flexural Properties through Fibre Prestressing , Journal of Reinforced Plastics and Composites, 18(3): 279-288 .

13.

Cao, Y. and Cameron, J. (2005). Flexural and Shear Properties of Silica Particle Modified Glass Fiber Reinforced Epoxy Composite , Journal of Reinforced Plastics & Composites, 25(4): 347-359 .

14.

Cao, Y. and Cameron, J. (2005). Impact Properties of Silica Particle Modified Glass Fiber Reinforced Epoxy Composite , submitted to Journal of Reinforced Plastics & Composites, 25(7): 761-769 .

15.

Lange, J. , Toll, S. , Manson, J. E. and Hult, A. (1995). Residual Stress Build-up in Thermoset Films Cured above Their Ultimate Glass Transition Temperature , Polymer, 36(16): 3135-3141 .

16.

Lange, J. , Toll, S. , Manson, J. E. and Hult, A. (1997). Residual Stress Build-up in Thermoset Films Cured below their Ultimate Glass Transition Temperature , Polymer, 38(4): 809-815 .

17.

Ochi, M. , Yamashita, K. and Shimbo, M. (1991). The Mechanism for Occurrence of Internal Stress during Curing Epoxide Resins , Journal of Applied Polymer Science, 43: 2013-2019 .

18.

Plepys, A. R. and Farries, R. J. (1990). Evolution of Residual Stresses in Three-dimensionally Constrained Epoxy Resing , Polymer, 31(10): 1932-1936 .

19.

Park, I. , Lee, D. and Nam, J. (2002). Equivalent Processing Time Analysis of Glass Transition Development in Epoxy/Carbon Fiber Composite Systems , Journal of Applied Polymer Science, 84: 144-145 .