Mechanical Performance of Hemp Fiber Polypropylene Composites at Different Operating Temperatures

Abstract

In order to quantify the effect of temperature on the mechanical properties of hemp fiber polypropylene composites, formulations containing 25% and 40% (by weight) hemp fiber were produced and tested at three representative temperatures of 256, 296, and 336 K. Flexural, tensile, and impact tests, as well as dynamic mechanical analysis, were performed and the reduction in mechanical properties were evaluated. Impact resistance was independent of temperature, whereas flexural and tensile properties were strongly affected. The highest reductions were observed in stiffness (modulus) values and flexural properties were reduced to a higher degree. The reductions in mechanical properties were well explained by a simple quadratic curve-fitting procedure applied to experimental data. Dynamic mechanical analysis revealed no change in glass transition temperature when the fiber content was increased but the composite material had better temperature resistance at higher fiber content. The results of the present study will be helpful in determining the end-use application of these composite materials.

Keywords

composites mechanical properties temperature hemp fiber polypropylene.

References

Clemons, C. ( 2002). Wood-plastic Composites in the United States-The Interfacing of Two Industries. Forest Product Journal, 52(6): 10-18.

Wolcott, M.P. ( 2001). Wood-plastic Composites, In: Buschow K. H. J., et al. (ed.), Encyclopedia of Materials: Science and Technology, pp. 9759-9763, Elsevier Press , New York.

Bledzki, A.K. , Fink, H.-P. and Specht, K. (2004). Unidirectional Hemp and Flax EP and PP-composites: Influence of Defined Fiber Treatments, Journal of Applied Polymer Science, 93: 2150-2156.

Beckermann, G. , Pickering, K.L. and Foreman, N.J. ( 2004). The Processing, Production and Improvement of Hemp-fibre Reinforced Polypropylene Composites Materials, In: Proceedings of the 2nd International Conference on Structure, Processing and Properties of Materials, pp. 57-65, Dhaka, Bangladesh.

Hepworth, D.G. , Hobson, R.N. , Bruce, D.M. and Farrent, J.W. (2000). The Use of Unretted Hemp Fiber in Composite Manufacture, Composites: Part A, 31: 1279-1283.

Schildmeyer, A.J. ( 2006). Temperature and Time Dependent Behaviors of a Wood-polypropylene Composite, Master’s Thesis, Washington State University .

Bathgate, R.G. , Wang, C.H. and Pang, F. (1997). Effects of Temperature on the Creep Behavior of Woven and Stitched Composites , Composite Structures, 38(1-4): 435-445.

Pooler, D.J. ( 2001). The Temperature Dependent Non-linear Viscoelastic Response of a Wood Plastic Composite, Master’s Thesis, Washington State University.

Kobbe, R.G. ( 2005). Creep Behavior of a Wood-polypropylene Composite , Master’s Thesis, Washington State University.

10.

ASTM D790-07 (2007). Standard Test Method for Flexural Properties of Unreinforced and Reinforced Plastics and Electrical Insulating Materials, ASTM Annual Book, Vol. 08.01.

11.

ASTM D-638-03 (2003 ). Standard Test Method for Tensile Properties of Plastics . ASTM Annual Book, Vol. 08.01.

12.

ASTM D256-06a (2006 ). Standard Test Methods for Determining the Izod Pendulum Impact Resistance of Plastics. ASTM Annual Book, Vol. 08.01.

13.

Tajvidi, M. ( 2005). Static and Dynamic Mechanical Properties of a Kenaf Fiber-wood Flour/Polypropylene Hybrid Composite, Journal of Applied Polymer Science, 98: 665-672.

14.

Tajvidi, M. ( 2003). Study on the Engineering and Viscoelastic Properties of Natural Fiber Thermoplastic Composites using Dynamic Mechanical Analysis (DMA), PhD Dissertation, Faculty of Natural Resources, University of Tehran, Karaj, Iran, p. 202.

15.

Chen, J. and Gardner, D.J. ( 2008). Dynamic Mechanical Properties of Extruded Nylon-wood Composites, Polymer Composites, 29(4): 372-379.