Prediction of Mechanical Properties of Mica-filled Epoxy Composite Using Various Mechanical Models

Abstract

This paper reports an investigation on the prediction of tensile properties of mica-filled epoxy composites. Various mechanical models were used to predict the tensile properties of mica-filled epoxy composites at several mica concentrations (5-30 vol%). The tensile properties of mica-filled epoxy at various mica contents were determined experimentally and modeled using Nielsen, Nicolais-Narkis, Verbeek, Halpin-Tsai, Guth, and Novak models. It was found that the tensile modulus of epoxy increases with increasing mica content, whereas the elongation at break and tensile strength decrease. Predictions, which have been offered by the models on tensile strength, elongation at break, and Young’s modulus, are in good agreement with experimental data over the range of mica contents studied. The Halpin-Tsai model shows best agreement in predicting the Young’s modulus (accuracy > 93 %), and Novak curve fitting shows best prediction for elongation at break (accuracy > 99%) for mica-filled composites. In the case of tensile strength, good agreement with Nicolais-Narkis models (accuracy > 99%) was obtained.

Keywords

polymer matrix composites (PMCs)mechanical properties analytical modeling.

References

Duan, H.L. , Yi, X. , Huang, Z.P. and Wang, J.A. ( 2007). Unified Scheme for Prediction of Effective Moduli of Multiphase Composites with Interface Effects: Part II-Application and Scaling Laws, Mechanics of Materials, 39(1): 94-103.

Kontou, E. ( 2007). Micromechanics Model for Particulate Composites, Mechanics of Materials, 39(7): 702-709.

Verbeek, C.J.R. and Focke, W.W. (2002). Modelling the Young’s Modulus of Platelet Reinforced Thermoplastic Sheet Composites, Composites Part A: Applied Science and Manufacturing, 33(12): 1697-1704.

Zhang, Z. and Friedrich, K. ( 2003). Artificial Neural Networks Applied to Polymer Composites: A Review, Composites Science and Technology, 63(14): 2029-2044.

Nicolais, L. and Narkis, M. ( 1971). Stress-Strain Behavior of Styrene-Acrylonitrile/Glass Bead Composites in the Glassy Region, Polymer Engineering and Science, 11(3): 194-199.

Nielsen, L.E. (1966). Simple Theory of Stress-Strain Properties of Filled Polymers, Journal of Applied Polymer Science, 10: 97-103.

Verbeek, C.J.R. (2003). The Influence of Interfacial Adhesion, Particle Size and Size Distribution on the Predicted Mechanical Properties of Particulate Thermoplastic Composites, Materials Letters, 57(13-14): 1919-1924.

Novak, I. , Krupa, I. and Chodak, I. ( 2003). Analysis of Correlation Between Percolation Concentration and Elongation at Break in Filled Electroconductive Epoxy-based Adhesives , European Polymer Journal, 39(3): 585-592.

Yan, W. , Lin, R.J.T. and Bhattacharyya, D. ( 2006). Particulate Reinforced Rotationally Moulded Polyethylene Composites - Mixing Methods and Mechanical Properties, Composites Science and Technology, 66(13): 2080-2088.

10.

Wu, Y.P. , Jia, Q.X. , Yu, D.S. and Zhang, L.Q. (2004). Modeling Young’s Modulus of Rubber-Clay Nanocomposites Using Composite Theories, Polymer Testing, 23(8): 903-909.

11.

Phillips, D.C. and Harris, B. (1977). Polymer Engineering Composites , pp. 108-159, Elsevier Applied Science, London.

12.

Ahmed, S. and Jones, F.R. ( 1990). A Review of Particulate Reinforcement Theories for Polymer Composites, Journal of Materials Science, 25: 4933-4942.

13.

Mallick, P.K. (2000). Particulate and Short Fiber Reinforced Polymer Composites, In: Kelly, A. and Zweben, C. (eds), Comprehensive Composite Materials, Vol. 2, p. 291, Elsevier Science Ltd, Oxford.

14.

Nielsen, R. ( 1974). Mechanical Properties of Polymers and Composites 2, pp. 378-450, Marcel Dekker Inc, New York.

15.

Rubin, I.I. ( 1990). Handbook of Plastic Materials and Technology, p. 394 , John Wiley & Sons, New York .

16.

Guz, I.A. , Rodger, A.A. and Rushchitsky , J.J. (2007). Developing the Mechanical Models for Nonmaterials, Composites Part A: Applied Science and Manufacturing, 38(4): 1234-1250.

17.

Bliznakov, E.D. , White, C.C. and Shaw, M.T. (2000). Mechanical Properties of Blends of HDPE and Recycled Urea-Formaldehyde Resin, Journal of Applied Polymer Science, 77(14): 3220-3227.

18.

Bose, S. and Mahanwar, P.A. ( 2005). Influence of Particle Size and Particle Size Distribution on Mica Filled Nylon 6 Composite, Materials Science, 40(24): 6423-6428.

19.

Bose, S. , Raghu, H. and Mahanwar, P.A. ( 2006). Mica Reinforced Nylon-6: Effect of Coupling Agents on Mechanical, Thermal, and Dielectric Properties, Applied Polymer Science, 100(5): 4074-4081.

20.

Rothon, R.N. ( 2002). Particulate Fillers for Polymers, pp. 350-400, Rapra Technology Ltd, UK.

21.

Vasconcelos, P.V. , Lino, F.J. , Van Hattum, F.W.J. and Neto, R.J.L. (2004). Mathematical Models for Particulate Filled and Milled Fibre Reinforced Composite, Materials Science Forum, 455-456: 742-745.

22.

Tsantzalis, S. , Karapappas, P. , Vavouliotis, A. , Tsotra, P. , Paipetis, A. , Kostopoulos, V. and Friedrich, K. (2007). Enhancement of the Mechanical Performance of an Epoxy Resin and Fiber Reinforced Epoxy Resin Composites by the Introduction of CNF and PZT Particles at the Microscale, Composites: Part A, 38(4): 1076-1081.