Effects of low-temperature treatments on surface hardness,retained austenite content,residual stress condition and the resulting tooth root bending strength of case-hardened 18CrNiMo7-6 gears
Restricted accessResearch articleFirst published online November, 2019
Effects of low-temperature treatments on surface hardness,retained austenite content,residual stress condition and the resulting tooth root bending strength of case-hardened 18CrNiMo7-6 gears
This paper contains parts of the research project FVA 612 and investigates the correlation between low-temperature treatments of case-hardened gears made from the material 18CrNiMo7-6 and the resulting surface hardness, retained austenite content, and residual stress condition. These parameters were further investigated with regard to the tooth root bending strength obtained with pulsating test rigs. The tested gears were subjected to various low-temperature treatments including different temperature levels before or after tempering. Other investigated parameters were the application of a shot blasting treatment and the effect of low-temperature treatments on gears with increased retained austenite content after the carburizing process.
Dobler F, Hoja T, Tobie T, et al. Tiefe Temperaturen - Einfluss von tiefen Temperaturen auf die Festigkeitseigenschaften einsatzgehärteter und verzahnter Bauteile. Forschungsvorhaben Nr. 612 (IGF-Nr. 16354 N), Abschlussbericht. Forschungsvereinigung Antriebstechnik e.V. (FVA), Frankfurt am Main, 2014.
2.
Leube H, Vogler J and Weck M. Randkohlenstoffgehalt - Einfluss des Randkohlenstoffgehaltes auf die Tragfähigkeit einsatzgehärteter Zylinderräder. Forschungsvorhaben Nr. 76 (AiF-Nr. 4792), Abschlussbericht Teil I. Forschungsvereinigung Antriebstechnik e.V. (FVA), Frankfurt am Main, 1987.
3.
Cavallaro GP. Fatigue properties of carburised gear steels. Dissertation, University of South Australia, Australia, 1995.
4.
AminiKAraghiAAkhbarizadehA. Effect of deep cryogenic heat treatment on the wear behaviour of carburized DIN 1.7131 grade steel. Acta Metall Sin2015; 28: 348–353.
5.
Babul T, Nakonieczny A and Ciski A. Effect of cold treatment or deep cryogenic treatment on selected properties of case-carburized 18CrNiMo7-6 steel. In: Proceedings of 18th IFHTSE congress, Rio de Janeiro, Brazil, 2010, pp.4179–4187.
6.
BenselyAPrabhakaranAMohan LalD, et al.Enhancing the wear resistance of case carburized steel (En 353) by cryogenic treatment. Cryogenics2006; 45: 747–754.
7.
BenselyAShyamalaLHarishS, et al.Fatigue behaviour and fracture mechanism, of cryogenically treated En 353 steel. Mater Des2009; 30: 2955–2962.
8.
BenselyAVenkateshSMohan LalD, et al.Effect of cryogenic treatment on distribution of residual stress in case carburized En 353 steel. Mater Sci Eng A2008; 479: 229–235.
9.
Jung S-C, Medlin DJ and Krauss G. Effect of subzero treatment on the bending fatigue performance of carburized SAE-4320 and SAE-9310 steels. SAE Technical Paper Series, 1996.
10.
KimCDiesburgDEBuckRM. Influence of sub-zero and shot-peening treatments on impact and fatigue fracture properties of case-hardened steels. J Heat Treat1981; 2: 43–53.
11.
Dobler F, Tobie T and Stahl K. Influence of low temperatures on material properties and tooth root bending strength of case-hardened gears. In: Proceedings of the ASME design engineering technical conference, Boston, Massachusetts, USA, 2015.
12.
Weigand U. Werkstoff- und Wärmebehandlungseinflüsse auf die Zahnfußtragfähigkeit. Dissertation, TU München, 1999.
13.
Norm ISO 6336, 2003/2006: Calculation of load capacity of spur and helical gears – Part 1-5, 2003/2006.
14.
HückM. Ein verbessertes Verfahren für die Auswertung von Treppenstufenversuchen. Zeitschrift für Werkstofftechnik1983; 14: 406–417.
15.
OilaALungCBullS. Elastic properties of eta carbide (n-Fe2C) from ab initio calculations: application to cryogenically treated gear steel. J Mater Sci2014; 49: 2383–2390.
16.
StrattonP. Cryogenic treatment of case hardened steel. Int Heat Treat Surf Eng2010; 4: 14–16.
17.
YenP-LKamodyDJ. Formation of fine eta carbides in special cryogenic and tempering process key to improved properties of alloy steels. Ind Heat1997; 64: 40–44.
18.
AbudaiaFBEvansJTShawBA. Characterization of retained austenite in case carburized gears and its influence on fatigue performance. Gear Technol2003; 20: 12–16.
19.
Güntner C, Tobie T and Stahl K. Influence of the residual stress condition on the load carrying capacity of case hardened gears. American Gear Manufacturers Association, AGMA Technical Paper 17FTM20, 2017.
20.
Höhn B-R, Tobie T, Stenico A, et al. Influence of residual stresses on tooth root bending strength of case hardened gears. In: Proceedings of the JSME international conference on motion and power transmissions, Matsushima Isles Resort, Japan, 2009, pp.333–337.
21.
König J, Koller P, Tobie T, et al. Correlation of relevant case properties and the flank load carrying capacity of case-hardened gears. In: Proceedings of the ASME design engineering technical conference, Boston, Massachusetts, USA, 2015.