Analysis of the effect of repair welding/grinding on the performance of railway crossings using field measurements and finite element modeling

Abstract

In this paper, the effects of repair welding and grinding, which are currently the main components used in the maintenance of crossings, on the performance of crossings are analyzed. It has been observed that sometimes the welding and grinding activities that directly affect the geometry of the crossings and/or material properties can have negative effects on the performance and ultimately on the service life of the crossings. In this paper, the effect of the changes of geometry has been studied experimentally, while the effect of the changes in the material properties has been analyzed using a numerical model. When grinding the shape of the crossing nose, the resulting profile can deviate from the original one. To analyze the geometry-related effects of welding and grinding, the geometry of crossings (cross-sectional profiles) as well as the corresponding dynamic accelerations due to passing trains are measured before and after the welding and grinding activities. Based on the comparison of the measured accelerations, the performance of the measured crossings has been assessed. Also, a welding repair that is not properly performed can lead to undesirable changes in the material properties of the rails, resulting in defects in rails. The material-related effects of the welding and grinding are studied using the three-dimensional explicit finite element model wherein a wheelset moves over a railway crossing. To understand the microstructure of the welding defect and provide an input for the numerical model, the results of ultrasonic and microscopic analyses of some welded crossings are presented first. Then, a number of the numerical simulations of the crossing with the welding defect are performed to investigate the failure mechanism of the crossing. Furthermore, assessment using the fatigue model (coupled with the finite element model) that accounts for the ratcheting behavior of material by calculating a number of the load cycles to the crack initiation is performed. Finally, conclusions on the effects of changes in geometry and material of the crossings due to repair welding and grinding are given.

Keywords

Railway turnout crossing wheel–rail contact explicit finite element modeling repair welding and grinding rolling contact fatigue

Get full access to this article

View all access options for this article.

References

Markine

Steenbergen

MJMM

Shevtsov

. Combatting RCF on switch points by tuning elastic track properties. Wear 2011; 271: 158–167.

Wan

Markine

Shevtsov

. Optimization of the elastic track properties of turnout crossings. J Rail Rapid Transit 2014; 230: 360–373.

Xiao

Zhang

Qian

. Numerical simulation of stress and deformation in a railway crossing. Eng Fail Anal 2011; 18: 2296–2304.

Pålsson

Nielsen

JCO

. Wheel–rail interaction and damage in switches and crossings. Veh Syst Dyn 2012; 50: 43–58.

Wang

Lian

et al.

Probabilistic prediction model for initiation of RCF cracks in heavy-haul railway. Int J Fatigue 2011; 33: 212–216.

Wan

Markine

Shevtsov

. Improvement of vehicle-turnout interaction by optimising the shape of crossing nose. Veh Syst Dyn 2014; 52: 1517–1540.

Palsson BA. Optimization of railway switches and crossings. PhD Thesis, Chalmers University of Technology, Sweden, 2014.

Markine

Wan

. Performance optimised geometry of railway crossings: Damage and implementation. Int J Railway Technol 2016; 5: 1–25.

Markine

Shevtsov

Experimental analysis of the dynamic behaviour of railway turnouts. In: BHV

Topping

(ed). The eleventh international conference on computational structures technology, Dubrovnik, Croatia: Civil-Comp Press, 2012.

10.

Markine VL and Shevtsov IY. An experimental study on crossing nose damage of railway turnout in the Netherlands. In: The fourteenth international conference on civil, structural and environmental engineering computing, 2013. Cagliari, Italy: Civil-Comp Press.

11.

Steenbergen M. Breukonderzoek geconstrueerde puntstukken WBN 1:15. Report Steenbergen Consulting, 2012.

12.

Zerbst

Madler

Hintze

. Fracture mechanics in railway applications: An overview. Eng Fract Mech 2005; 72: 163–194.

13.

Cui

Tan

. Metallography and hear treatment (in Chinese), China: Harbin Institute of Technology Press, 2010.

14.

Capdevila

Caballero

Garcia De Andres

. Determination of Ms temperature in steels: A Bayesian neural network model. ISIJ Int 2002; 42: 894–902.

15.

Sourmail

Garcia-Mateo

. Critical assessment of models for predicting the Ms temperature of steels. Comput Mater Sci 2005; 34: 323–334.

16.

Andrews

. Empirical formulae for the calculation of some transformation temperatures. JISI 1965; 203: 721–727.

17.

Xin

Markine

Shevtsov

. Numerical analysis of the dynamic interaction between wheelset and turnout crossing using explicit finite element method. Veh Syst Dyn 2016; 54: 201–327.

18.

Lance J. Lab report: Heat treatment of steel, http://www.csus.edu/wac/journal/2012/lance_final_draft.pdf.

19.

Mahendran M. The modulus of elasticity of steel – is it 200GPa? In: Thirteenth international specialty conference on cold-formed steel structures, St. Louis, MO, USA, 17–18 October 1996.

20.

Zhang

. General relationship between strength and hardness. Mater Sci Eng A 2011; 529: 62–73.

21.

Sundström

Rendóna

Olsson

. Wear behavior of some low alloyed steels under combined impact/abrasion contact conditions. Wear 2001; 250: 744–754.

22.

LS-DYNA_manual_Vol_II_R7.1 material, 2014.

23.

Lewis R and Olofsson U. Wheel-rail interface handbook. UK: Woodhead Publishing Limited, 2009.

24.

Ringsberg

Loo-Morrey

Josefson

et al.

Prediction of fatigue crack initiation for rolling contact fatigue. Int J Fatigue 2000; 22: 205–215.

25.

Jiang

Sehitoglu

. A model for rolling contact failure. Wear 1999; 224: 38–49.

26.

Kapoor

. A re-evaluation of the life to rupture of ductile metals by cyclic plastic strain. Fatigue Fract Eng Mater Struct 1994; 17: 38–49.

27.

Norberg L. Fatigue properties of austenitic Mn-steel in explosion depth hardened condition. Master Thesis, Chalmers University of Technology, 2010.

28.

EN13674-1. Railway applications – Track – Rail – Part 1: Vignole railway rails 46kg/m and above.