Preparation of inexpensive modified polystyrene with adipoyl chloride and N-benzimidazole iminoesther for the removal of Ni 2+ and study of the impedance and conductivity of the obtained complex

Abstract

We used, in this work, a potentially effective adsorbent for removing nickel (Ni²⁺) from wastewater, employing modified polystyrene; the di-acylated polystyrene with iminoether (DIPS-N-Ac-Imi). The product was utilized for the adsorption of Ni(II) from waste water at ambient temperature. The di-acylated polystyrene with iminoether DIPS-N-Ac-Imi and DIPS-N-Ac-Imi/Ni²⁺ were characterized using infrared spectroscopy (FT-IR), thermogravimetry, and X-ray diffraction (XRD). Subsequently, the percentage of adsorption of DIPS-N-Ac-Imi/Ni²⁺ was determined via atomic absorption spectroscopy. An electrical study of DIPS-N-Ac-Imi/Ni²⁺ was performed using Impedance Spectroscopy, revealing a stimulated thermal conduction mechanism. Based on conductivity analyses, the activation energy was deduced from the Arrhenius diagram and corresponded to Ea = 1.07 eV, which suggests that DIPS-N-Ac-Imi/Ni²⁺ is a proton-type semiconductor.

Keywords

Modified polystyrene DIPS-NH-Ac-Imi/ Ni2+Impedance Semiconductor

Introduction

Ni(II) is one of the most toxic metals, it belongs to a broad category of persistent environmental pollutants like Hg(II), Pb(II), and Cr(VI). It’s is a primary water pollutant in aquatic environments due to its harmful effects on living organisms and its inability to degrade naturally.^1,2 Once individuals are confronted with elevated amounts of nickel contaminating the environment, many diseases can affect humans, including pulmonary fibrosis, cardiovascular problems, and cancer.³ Water polluted by heavy metals, such as Ni²⁺, poses a significant problem due to its toxicity. Numerous methods have been used to remove Ni(II), including ion exchange, membrane separation, flotation, osmos inverse, electrocoagulation from wastewater.^4–9 A wide range of modified polystyrene have been utilized for heavy metal removal.^10–14

In fact, incorporating transition metals to organic ligand improves their electrical properties. From where more attention has been devoted to studying the conductivity and electrical properties of modified polystyrene.^14,15

The chemical modification of the polystyrene structure involves reactions on the benzene ring nucleus. Consequently, this functionalization gives rise to new derivatives, which serve to widen the fields of use of polystyrene (PS). The purpose of functionalized polystyrene is to enhance its properties and to further expand its possible uses, particularly by altering the type and quantity of functional groups present in the modified polystyrene. For example, functionalizing polystyrene increases its resistance to metal corrosion.¹⁶ Furthermore, polystyrene nanocomposites can be obtained with desired properties. For example, they can improve thermal stability and flammability.¹⁷ They can be used to synthesize silver nanoparticles in aminated polystyrene-functionalized cells; the resulting compound is a highly reactive nanocomposite, whose catalytic activity has been demonstrated through methylene blue reduction.¹⁸ The PS-metformin/CuCl₂ complex exhibits antibacterial activity and simultaneously acts as a recyclable nanocatalyst in indole and aniline N-arylation reactions. These special properties make it increasingly valuable in various fields of application.^19,20

However, according to our research, no previous studies mention the use of N-acylated substituted by iminoesther modified polystyrene for the Ni(II) elimination from wastewater, and the electrical properties of DIPS-NH-Ac-Imi/Ni²⁺, have not been reported yet.

The principal goal of this work is to use an inexpensive method for removing Ni(II) ions from waste water by utilizing our modified polystyrene as an adsorbent, knowing that the proposed method has been used successfully in order to remove Ni²⁺ from wastewater. Subsequently, we will report the impedance and conductivity of the obtained DIPS-NH-Ac-Imi/Ni²⁺ derived from polystyrene complexes.

Experimental

General considerations

The following materials were used for the synthesis and analysis of this study. The polystyrene utilized in this investigation is a commercially available linear with a molecular weight of MW of DIPS = 350,000 g.mol⁻¹. Orthoester (EtC(OEt)₃), 2-aminobenzimidazole (1H-benzimidazol-2-amine) and Stannous chloride (SnCl₂, 99.99%), were obtained from Fluka (FLUktuierendeKAskade, France) and used without any further purification. Nitric acid (HNO₃, 86%), chloroform (CHCl₃, 99%), absolute ethanol (EtOH), hydrochloric acid (HCl, 37%), methanol (MeOH) sulfuric acid (H₂SO₄, 95%–98%), chloroform (CHCl₃, 99%) and were purchased from Sigma Aldrich (formally Millipore Sigma, France) and used as-received.

The wastewater collection was carried out in the first week of March 2023. It’s collected from waste water of stainless-steel manufacturing, and storage battery industries, its color is yellow with turbidity. Wastewater sampling was carried out by placing the 1L flask capacity in the basin at a depth of 10 cm. Before treatment with polymers, the sample was kept and filtered at 25°C.

Synthesis of amino polystyrene

The method used for the preparation of amino polystyrene was adopted from a previous study.¹⁴

Preparation of N-acylated polystyrene

Synthesis of di-polystyrene acylated: (DIPS-NH-Ac)

To 1.0 g of aminated polystyrene dissolved in toluene, we add 1.0 mL of adipoylchloride (C₆H₈Cl₂O₂) in THF dropwise. The mixture is then heated under reflux for 24 h. The resulting product is filtered and washed with ether.

Synthesis of di-polystyrene acylated with iminoether: (DIPS-N-Ac-Imi)

N-2-benzimidazoyl Iminoether was prepared using a method from previous work.¹⁴ 0.5 g of N-acylated polystyrene was dissolved in a small amount of ethanol, then 1.0 g of iminoether was added, and the mixture was heated using a microwave for 1 h. The product obtained was filtered and dried. The colors of different compounds are presented in Figure 1.

Figure 1.

(a) DIPS-NH₂; (b) DIPS-NH-Ac and (c) DIPS-N-Ac-Imi.

Extraction of Ni²⁺ located in wastewater

0.1 g of DIPS-N-Ac-Imi polymer was incubated with 20.0 mL of wastewater and left at room temperature for 24 h. The resulting mixture was filtered and washed with demineralized water (3 × 50.0 mL), the solid phase was washed with 30.0 mL of distillated water at T = 50°C during 20 mn for desorption of Ni²⁺ retained by studied polymers. The obtained aqueous phase was analyzed by atomic absorption spectroscopy for dosing the amount of removal Ni²⁺.

We have repeated the extraction 3 times we have obtain the same dosage.

Characterization methods

FTIR spectroscopy, X-ray diffractometer, TGA, DTA, atomic absorption were employed for comprehensive characterization.

FTIR

They were enregistred using A Nicolet Infrared Spectrometer IR–200 FT-IR (Thermo Fisher Scientific, USA) was employed to determine the different functional groups present in the polystyrene derivatives. The attenuated total reflectance (ATR) mode was utilized in the range of 4000 and 400 cm⁻¹, with a measurement accuracy of approximately 4 cm⁻¹.

XRD

We used X-ray diffraction patterns which were carried out using a Bruker D8-Advance diffractometer furnished with a vertical goniometer type accelerator and operating with (CuKα) = 1.54,059 Å) to obtain X-ray diffraction (XRD) scans. Typically, slow measurements were performed in angular ranges from 5 to 120° with a step size of 0.01°2θ and average acquisition times of 2 h.

Atomic absorption

Atomic absorption spectroscopy uses the property of certain chemical elements to capture or emit light (UV and/or visible) when heated to a very high temperature in a flame or in an oven. The quantity of metal ions attached to the synthesized polymers was determined through atomic absorption spectroscopy analysis using an analysis Perkin–Elmer AAnalyst 200, with calibration performed using solutions of the studied metal ranging from 0.5 to 5 mg/dm³.

TGA and DTA

TGA and DTA were conducted using a thermal analyzer (Perkin Elmer STA 6000, USA) with N₂ circulation and a gradual heating rate of 5°C per minute from room temperature up to 450°C. This technique allowed us to observe changes in product stability at elevated temperatures.

Impedance

The impedance analysis was performed using a Hewlett-Packard 4192A impedance analyzer, covering the frequency range from 5 Hz to 13 MHz.

Results and discussion

FTIR

The FTIR spectra of the compounds are presented in Figure 2.

Figure 2.

FT-IR spectra of (a) PS-NH₂; (b) DIPS-NH-Ac; (c) DIPS-N-Ac-Imi and (d) DIPS-N-Ac-Imi/Ni²⁺.

The characteristic bands corresponding to the various functional groups DIPS in DIPS-NH-Ac, DIPS-N-Ac-Imi, and the complex DIPS-N-Ac-Imi/Ni²⁺.In curve (a), the spectrum of DIPS-NH-Ac shows the appearance at 1644 cm⁻¹ a band that corresponded to C=N of iminoether which proves the insertion of N-2-iminoether. Comparing the FTIR spectrum of DIPS-N-Ac-Imi (curve c) and the spectrum of DIPS-N-Ac-Imi/Ni²⁺(curve d), we notice that some peaks intensities have changed due to the adsorption of Ni²⁺. The adsorption primarily influenced the vibrations of (C=O) and (C=N) bands, as well as the nitrogen atoms’ free doublets. We conclude then the Ni²⁺ displays excellent interaction into the doublets of N atoms in iminoether and the NH of the functionalized amine polystyrene derivatives.^14,18

X-ray diffraction

The pattern resulting from X-ray diffraction of PS-NH₂, DIPS-NH-Ac(dipolystyrene-NH-acylated), DIPS-N-Ac-Imi, DIPS-N-Ac-Imi/Ni²⁺ and iminoether are presented in Figure 3. The X-ray exhibits sharp and diffuse peaks. Sharp peaks corresponded to crystalline structure of iminoether, while the X-ray pattern of DIPS-NH-Ac, DIPS-N-Ac-Imi, DIPS-N-Ac-Imi/Ni²⁺ presents diffuse peaks, indicating that the modified polymer have an amorphous structure.

Figure 3.

X-ray diffraction patterns of (a) PS-NH₂; (b) DIPS-NH-Ac; (c) DIPS-N-Ac-Imi; d) DIPS-N-Ac-Imi/Ni²⁺ and (e) iminoether.

The patterns of DIPS-NH-Ac (b) presented many sharp peak, at 10, 11, 15, 17, 21, 23 and 27 (2θ), and the patterns of DIPS-N-Ac-Imi (c) compared to DIPS-NH-Ac showed the disappearance of peaks at 10, 17 and 21 (2θ) and exhibits new peaks at 19, 34, 51. Upon complexing the modified PS with Ni²⁺, the X-Ray diffraction pattern showed the disappearance of peaks at 19, 23, 27 and 51 compared to the pattern of DIPS-N-Ac-Imi.

TGA and DTA

TGA analysis of all compounds is performed to identify changes in weight and temperature. The thermograms of TGA and DTA of DIPS-NH-Ac and DIPS-N-Ac-Imi show an exothermic undergo a two-step decomposition process. At around 350°C and 375°C the first step for DIPS-NH-Ac and DIPS-N-Ac-Imi, respectively, and the second step of decomposition process starts at around 475°C for DIPS-NH-DIAC and 520°C and DIPS-N-Ac-Imi. The decomposition temperature has increased going from DIPS-NH-Ac to DIPS-N-Ac-Imi so we can note that the polymer has become more stable and its thermal decomposition properties have been improved. Whereas when the DIPS-N-Ac-Imi is complexed by Ni²⁺, we note the appearance of new peaks around 240, as well as the decrease in intensity of the second decomposition peak which is explained by the effect of Ni²⁺ on the product. The thermograms of DTA/TGA of DIPS-N-Ac-Imi/Ni²⁺ present at around 200 and 300°C, an endothermic peak with mass loss, that can be attributed to the pyrolysis of DIPS-N-Ac-Imi/Ni²⁺. (Figure 4)

Figure 4.

TGA/DTA of (a) DIPS-NH-Ac, (b) DIPS-N-Ac-Imi and (c) DIPS-N-Ac-Imi/Ni²⁺.

Atomic absorption

Atomic absorption spectrometry (AAS) is a technique used to determine the concentration of certain metals in a sample.

The atomic absorption technique was used in order to evaluate the extraction rate of metals. The results were presented as percentages of metal extraction, based on its initial concentration. The assessment of metal removal percentage was performed using the subsequent equation:

% Extraction = (\frac{C_{0} - C_{i}}{C_{0}}) * 100

C₀: metal concentration in the waste water prior to extraction, C_i: metal concentration determined posterior to extraction.

The extraction of Ni²⁺ using and DIPS-N-Ac-Imi, was carried out in the waste waters of Ni.

We studied the influence of the concentration of the extraction agent on the extraction of Ni(II) ions to see the maximum extraction percentage. We varied the concentration of the modified polymer in the range of 1.0 to 10% (v/v) in water as a diluent. Maximum extraction (98%) was achieved with 7.0% modified polymer in water. Therefore, the percentage of metal extracted can be considered a response to the percentage of active extractant in the diluent.

Figure 5 illustrates the structure of the DIPS-N-Ac-Imi/Ni ²⁺.

Figure 5.

Scheme of complexation of the modified polystyrene by Ni²⁺.

Elementary analysis

The chemical composition of the synthesized polymers was determined at each stage of synthesis by means of comprehensive elemental analyses, enabling the constituent elements of the polymers to be identified and quantified at different stages of their formation. Each stage of the synthesis was meticulously studied to characterize the changes occurring in the chemical composition of the polymers during their formation. These analyses provided crucial data on the elements present in the samples at different stages of the synthesis process. The results are presented as N/C ratios in Figure 6. The N/C value of aminated polystyrene (PS-NH₂) is around 0.09. The degree of substitution of PS by amine groups was calculated as above 90% from the following equation, by considering the generic formula: (C₈H₁₀)_n-(NH₂)_n

with n = (104 \times N %) / (1400 - 45 \times N %),

where N% is the percentage of nitrogen per unit mass determined by elemental analysis. After condensation with adipoyl chloride, the N/C ratio is 0.085. Following grafting with N-2-benzimidazoyl iminoether, the N/C value increased to around 0.14, since it is rich in nitrogen and carbon atoms. These data are in perfect agreement with the chemical structures of the PS-NH₂ samples DIPS-NH-Ac and DIPS-N-Ac-Imi.

Figure 6.

Nitrogen/carbon atomic ratios as given by elemental analysis for PS-NH₂, DIPS-NH-Ac and DIPS-N-Ac-Imi.

In summary, the determination of the chemical composition of synthesized polymers at each stage of synthesis has enabled a thorough understanding of the molecular evolution and chemical transformations that occur throughout the manufacturing process. These results provide a solid basis for characterizing and optimizing the properties of the polymers obtained.

All these results reveal the success of the chemical modification of polystyrene and the obtention of new polymeric derivatives with potential chelating properties towards metal ions, including Nickel.

Impedance

Complex impedance spectroscopy is a potent, non-destructive analysis methodology; extensively employed across various research domains such as microelectronics, electrical engineering and material physics. The complex impedance is expressed as:

Z^{*} = Z^{'} - j Z^{″}

and the result is visualized as a Nyquist graph, where the abscissa of a Cartesian coordinate system corresponds to the real part of the transfer function is plotted on the X axis of the impedance and the Y-axis represents the plotted imaginary part.

The complex impedance of DIPS-N-Ac-Imi/Ni²⁺ was studied using an analyzer Hewlett-Packard 4192A impedance, within the frequency span from 5 Hz to 13 MHz. Figure 7 represents the Nyquist graphs of DIPS-N-Ac-Im/Ni²⁺ at temperatures going from 582°K to 603°K. The resulting curves take the form of semicircles, corresponding to an equivalent circuit made up of a combination of a constant phase element, CPE, and a bulk resistance, Rb.

Figure 7.

Nyquist plot of DIPS-N-DIAC-Im/Ni²⁺ depending on temperature.

As the temperature rises, the diameters of the semicircles decrease, showing the presence of an activated thermal conduction mechanism.²¹ The bulk resistance values at different temperatures are determined by extracting the intercept of the semicircular arc on the real axis (Z′. axis).

Figure 8 illustrates the frequency dependencies of the real parts of the impedance of DIPS-N-Ac-Imi/Ni²⁺, at various temperatures. For all the temperatures, Z′ remained almost constant at low frequencies and then decreased in magnitude for frequencies above 10⁴ to nearly vanish at 10⁵. The low Z′ values at high frequencies are due to the fact that the space charges are more energetic at high frequencies and can overcome the barrier height.

Figure 8.

Frequency dependence of the real part of Z′ the complex impedance of DIPS-N-DIAC-Im/Ni²⁺ at different temperatures.

As observed in Figure 9, it shows the frequency dependence of the imaginary part, Z″, of DIPS-N-Ac-Imi/Ni²⁺ at different temperatures. Each temperature showed a single peak (Z″_max), confirming the single semicircle shape of the Nyquist plot.²²Additionally, it was noted that as the temperature increased, the frequency of this peaks changed to higher values, which accurately represent a relaxation process²³ in the produced DIPS-NH-Ac-Imi/Ni²⁺.

Figure 9.

Frequency dependence of the imaginary part of Z″ the complex impedance of DIPS-N-DIAC-Im/Ni²⁺ at different temperatures.

Conductivity analysis

The conductivity of DIPS-N-Ac-Imi/Ni²⁺ was performed by using a pellet with a geometric factor $g = e / S = 0.101 {c m}^{- 1}$ , where S and e are the contact surface area of the sample, and the thickness, respectively. The conductivity, σ, and the resistance, R, of the sample were then calculated from the equation $σ = g / R$ .

Figure 10 displays an Arrhenius plot within the temperature range of 582 K to 603 K, demonstrating that the plot of ln(σT) relatives to 1000/T was linear, with an excellent correlation coefficient (R² > 0.995), confirming the presence of an Arrhenius type behavior:

Ln (σ T) = - \frac{E_{a}}{K T} + Ln (A)

where A is a material-depend constant, K is the constant of Boltzmann, and

E_{a}

is the activation energy. Consequently, the activation energy was determined from the Arrhenius plot,

E_{a} = 1, 07 e V

, indicating a proton-type semiconductor type of DIPS-N-Ac-Imi/Ni²⁺.

Figure 10.

Arrhenius plot of DIPS-N-Ac-Imi/Ni²⁺.

Conclusions

Aminated polystyrene was initially modified using adipoyl chloride. Subsequently, it was reacted with iminoesther to enhance its performance in removing Ni²⁺ions from contaminated water. The complexation of DIPS-N-Ac-Imi with nickel metal was investigated in order to eliminate Ni(II) ions out of the waste water.

The adsorption capacity and removal efficiency of the prepared adsorbent (DIPS-N-Ac-Imi) were confirmed by atomic adsorption. Infrared spectroscopy (FT-IR) was used to identify the different polymers obtained. X-ray diffractometry (XRD) analysis was conducted and shows that the structure of our polymer is amorphous. The differential thermal analysis (DTA) were utilized to investigate the thermal stability and structure of the modified polystyrene and the polystyrene with nickel metal, respectively.

Through the analysis of conductivity and impedance of DIPS-N-Ac-Imi/Ni²⁺, we noticed that this compound exhibits semiconductor properties as a functionalized polymer.

Footnotes

Acknowledgements

The authors would like to acknowledge the support from the Ministry of High Education of Tunisia for financial of this work.

Declaration of conflicting interests

The author(s) declared no potential conflicts of interest with respect to the research, authorship, and/or publication of this article.

Funding

The author(s) disclosed receipt of the following financial support for the research, authorship, and/or publication of this article: This work was supported by University of Carthage.

ORCID iD

Ben Smida Nourhene

References

Taseidifar

Makavipour

Pashley

, et al. Removal of heavy metal ions from water using ion flotation. Environ Technol Innov 2017; 8: 182–190.

Khelifi

Nacef

Affoune

. Biosorption of Nickel (II) ions from waste waters by using chicken eggshells as low-cost biosorbent. Algerian J Environ Sci Technol 2016; 2: 33–37.

Coman

Robotin

Ilea

. Nickel recovery/removal from industrial wastes: a review. Resour Conserv Recycl 2013; 73: 229–238.

Wang

. Removal of heavy metal ions from wastewaters: a review. J Environ Manag 2011; 92: 407–418.

Khelifi

Nacef

Chelaghmia

, et al. Equilibrium, mechanism, and mass transfer studies of nickel(II) adsorption by sewage sludge-derived activated carbon. Iran J Chem Chem Eng 2021; 40: 1675–1682.

Naskar

Majumder

Goswami

, et al. Implication of greener biocomposite bead for decontamination of nickel (II): column dynamics study. J Polym Environ 2020; 28: 1985–1997.

Jiang

Yang

Huang

, et al. Removal of the heavy metal ion nickel (II) via an adsorption method using flower globular magnesium hydroxide. J Hazard Mater 2019; 373: 131–140.

Dermentzis

Christoforidis

Valsamidou

Loucas

. Removal of nickel, copper, zinc and chromium from synthetic and industrial wastewater by electrocoagulation. Int J Environ Sci 2011; 1: 697e710.

Heidmann

Calmano

. Removal of Zn(II), Cu(II), Ni(II), Ag(I) and Cr(VI) present in waste waters by aluminium electrocoagulation. J Hazard Mater 2008; 152: 934e941.

10.

Gonsalvesh

Marinov

Gryglewicz

, et al. Preparation, characterization and application of polystyrene based activated carbons for Ni(II) removal from aqueous solution. Fuel Process Technol 2016; 149: 75–85.

11.

Yang

Huang

Yao

, et al. Thiourea modified hyper-cross-linked polystyrene resin for heavy metal ions removal from waste waters. J Appl Polym Sci 2018; 135: 45568.

12.

Sun

Tang

, et al. Adsorption mechanism of cadmium on polystyrene microplastics containing hexabromocyclododecane. Environ Technol Innov 2021; 24: 102036.

13.

Chen

Wei

, et al. Adsorption of Cu²⁺ by UV aged polystyrene in waste water. Ecotoxicol Environ Saf 2022; 232: 113292.

14.

Ben Smida

Othmani

Abderrahim

. The study of impedance and conductivity of new modified polystyrene used as an effective adsorbent of Ba(II) ions. Chem Biodivers 2023; 20: 202201150.

15.

Jabur

. Electrical and optical properties modification of polystyrene by Vanadium (V) ion-pair organometallic complex. Adv Nat Appl Sci 2015; 6: 1–6.

16.

Kurbanova

Mirzaoglu

Kurbanov

, et al. Functionalization of polystyrene and adhesion studies. J Adhes Sci Technol 1997; 11(1): 105–112.

17.

Katancic

Travaš-Sejdić

Hrnjak-Murgić

. Study of flammability and thermal properties of high-impact polystyrene nanocomposites. Polym Degrad Stabil 2011; 96: 2104–2111.

18.

Amari

Guerrouache

Mahouche‐Chergui

, et al. In situ synthesis of silver nanoparticles on densely amine-functionalized polystyrene: highly active nanocomposite catalyst for the reduction of methylene blue. Polym Adv Technol 2018; 30: 320–328.

19.

Veisi

Ahmadia

Mirshokraie

, et al. CuCl₂ heterogenized on metformine‐modified polystyrene resin as an antibacterial agent and recyclable nanocatalyst for Ullmann‐type C‐N coupling reactions. Appl Organomet Chem 2019; 33: 4737.

20.

Muwaffak

Fei

Isaac

. Exposure routes and health effects of heavy metals on children. Biometals 2019; 32: 563–573.

21.

Trabelsi

Harizi

Kanzari

. Complex impedance spectroscopy of Sn₄Sb₆S₁₃ thin films deposited by thermal vacuum evaporation. Thin Solid Films 2017; 631: 161–171.

22.

Zhou

Zhai

, et al. Novel barium titanate based ferroelectric relaxor ceramics with superior charge-discharge performance. J Eur Ceram Soc 2018; 38: 4646–4652.

23.

Hkiri

Salem

Othmani

, et al. Electrical and dielectric properties study of CaZrO₃-CaTiO₃ composite system by impedance spectroscopy. Ionics 2020; 26: 5099–5111.

Preparation of inexpensive modified polystyrene with adipoyl chloride and N-benzimidazole iminoesther for the removal of Ni 2+ and study of the impedance and conductivity of the obtained complex

Abstract

Keywords

Introduction

Experimental

General considerations

Synthesis of amino polystyrene

Preparation of N-acylated polystyrene

Synthesis of di-polystyrene acylated: (DIPS-NH-Ac)

Synthesis of di-polystyrene acylated with iminoether: (DIPS-N-Ac-Imi)

Extraction of Ni2+ located in wastewater

Characterization methods

FTIR

XRD

Atomic absorption

TGA and DTA

Impedance

Results and discussion

FTIR

X-ray diffraction

TGA and DTA

Atomic absorption

Elementary analysis

Impedance

Conductivity analysis

Conclusions

Footnotes

Acknowledgements

Declaration of conflicting interests

Funding

ORCID iD

References

Extraction of Ni²⁺ located in wastewater