This article presents the findings from a parametric study examining the effect of four contaminants (soot, oxidation, moisture, and sulphuric acid) at varying levels (four for each). It was observed that all contaminants and contaminant levels reduce the conductivity of the oil. Oxidation and soot contaminants produced large increases in viscosity. The wear rate was mainly influenced by acid and soot additions, while the coefficient of friction was increased by all contaminants and contaminant levels. The steady-state charge levels changed for some contaminants. The best correlation of steady-state charge with the other measured tribological parameters of wear rate, friction, and temperature is seen for the series of oxidized oils. The multi-contaminated oil (L4 × 4) shows remarkably little degradation in tribological performance. Analysis of the wear mechanisms shows that soot and oxidation produced abrasion and polishing wear, respectively, while sulphuric acid and moisture produced corrosive wear.
WarrensC.JefferiesA. C.MuftiR. A.LambG. D.GuiducciA. E.SmithA. G.Effect of oil rheology and chemistry on journal-bearing friction and wear. Proc. IMechE, Part J: J. Engineering Tribology, 2008, 222(3), 441–450.
2.
Needleman, W. M. and Madhavan P. V. Review of lubricant contamination and diesel engine wear. SAE paper 881827, 1988.
3.
AldajahS.AjayiO. O.FenskeG. R.GoldblattI. L.Effect of exhaust gas recirculation (EGR) contamination of diesel engine oil on wear. Wear, 2007, 263, 93–98.
4.
GautamM.ChitoorK.DurbhaM.SummersJ. C.Effect of diesel soot contaminated oil on engine wear - investigation of novel oil formulations. Tribol. Int., 1999, 32(12), 687–699.
5.
Snelling, D. R., Smallwood, G. J., Sawchuk, R. A., Neill, W. S., Gareau, D., Chippior, W. L., Gülder Ö. L., and Bachalo, W. D. Particulate matter measurements in a diesel engine exhaust by laser-induced incandescence and the standard gravimetric procedure. SAE paper 1999-01-3653, 1999.
6.
TruhanJ. J.QuJ.BlauP. J.The effect of lubricating oil condition on the friction and wear of piston ring and cylinder liner materials in a reciprocating bench test. Wear, 2005, 259(7–12), 1048–1055.
7.
OliverA. V.Gear lubrication – a review, Proc. IMechE, Part J: J. Engineering Tribology, 2002, 216(5), 255–267.
8.
SmiechowskiM. F.LvovichV. F.Electrochemical monitoring of water-surfactant interactions in industrial lubricants. J. Electroanal. Chem., 2002, 534(2), 171–180.
9.
MurakamiY.Analysis of corrosive wear of diesel engines: relationship to sulfate ion concentrations in blowby and crankcase oil. JSAE Rev., 1995, 16(1), 43–48.
10.
SinghS. K.AgarwalA. K.SrivastavaD. K.SharmaM.Experimental investigation of the effect of exhaust gas recirculation on lubricating oil degradation and wear of a compression ignition engine. ASME J. Eng. Gas Turbines Power, 2006, 128, 921–927.
11.
AkiyamaK.ManunagaK.KadoK.YoshiokaT.Cylinder wear mechanism in an EGR-equipped diesel engine and wear protection by engine oil. SAE paper 872158,, 1987.
12.
BowmanW. F.StachowiakG. W.Determining the oxidation stability of lubricating oils using sealed capsule differential scanning calorimetry (SCDSC). Tribol. Int., 1996, 29(1), 27–34.
13.
GraciaN.ThomasS.BazinP.DuponchelL.Thibault-StarzykF.LerasleO.Combination of mid-infrared spectroscopy and chemometric factorization tools to study the oxidation of lubricating base oils. Catal. Today, 2010, 155(3–4), 255–260.
14.
SharmaB. K.StipanovicA. J.Development of a new oxidation stability test method for lubricating oils using high-pressure differential scanning calorimetry. Thermochim. Acta, 2003, 402, 1–18.
15.
IsaF. M.Haji-SulaimanM. Z.An investigation of the relationship between used engine oil properties and simulated intake valve deposits. Proc. IMechE, Part D: J. Automobile Engineering, 1997, 211(5), 379–389.
16.
HarveyT. J.MorrisS.WangL.WoodR. J. K.PowrieH. E. P.Real-time monitoring of wear debris using electrostatic sensing techniques. Proc. IMechE, Part J: J. Engineering Tribology, 2007, 221(1), 27–40.
17.
HarveyT. J.WoodR. J. K.DenuaultG.PowrieH. E. G.Effect of oil quality on electrostatic charge generation and transport. J. Electrostat., 2002, 55(1), 1–23.
18.
HarveyT. J.WoodR. J. K.DenuaultG.PowrieH. E. G.Investigation of electrostatic charging mechanisms in oil lubricated tribo-contacts. Tribol. Int., 2002, 35(9), 605–614, 0301–679X.
19.
MorrisS.WoodR. J. K.HarveyT. J.PowrieH. E. G.Use of electrostatic charge monitoring for early detection of adhesive wear in oil lubricated contacts. J. Tribol. Trans ASME, 2002, 124(2), 288–296.
20.
TasbazO. D.WoodR. J. K.BrowneM.PowrieH. E. G.DenualtG.Electrostatic monitoring of oil lubricated sliding point contacts for early detection of scuffing. Wear, 1999, 230(1), 86–97.
21.
WangL.WoodR. J. K.HarveyT. J.MorrisS.PowrieH. E. G.CareI.Wear performance of oil lubricated silicon nitride sliding against various bearing steels. Wear, 2003, 255, 657–668.
22.
WangL.WoodR. J. K.HarveyT. J.MorrisS.PowrieH. E. G.CareI.Electrostatic monitoring of oil lubricated ceramic to steel contacts. Tribol. Res. Des. Eng. Syst., 2003, 41, 625–635.
23.
WangL.WoodR. J. K.CareI.PowrieH. E. G.Electrostatic wear sensing of ceramic-steel lubricated contacts. In Tribology and Interface Engineering Series, Transient processes in tribology, Proceedings of the 30th Leeds–Lyon Symposium on Tribology, 2003, pp. 711–720 (Elsevier).
24.
BoothJ. E.NelsonK. D.HarveyT. J.WoodR. J. K.WangL.PowrieH. E. G.MartinezJ. G.The feasibility of using electrostatic monitoring to identify diesel lubricant additives and soot contamination interactions by factorial analysis. Tribol. Int., 2006, 39(12), 1564–1575.
25.
BoothJ. E.HarveyT. J.WoodR. J. K.PowrieH. E. G.Advances in electrostatic health monitoring of tribo-contacts. In Proceedings of the IMechE Tribology Group 50th Anniversary Conference onTribology 2006: Surface engineering and tribology for future engines and drivelines, 12–13 July 2006, London, UK.
26.
Wood, R. J. K., Ramkumar, P., Wang, L., Harvey, T. J., Nelson, K., Yamaguchi, E. S., Harrison, J. J., Powrie, H. E. G., and Otin, N. Electrostatic monitoring of the effects of carbon black on lubricated steel/steel sliding contacts. In Tribology and Interface Engineering Series, Life cycle tribology – Proceedings of the 31st Leeds–Lyon Symposium on Tribology, Trinity and All Saints College, Horsforth, Leeds, UK, 7–10 September 2004, 2005, pp. 109–121, 1572–3364 (Elsevier).
27.
WangL.WoodR. J. K.The influence of contact conditions on surface reaction layers formed between steel surfaces lubricated by an aviation oil. Tribol. Int., 2007, 40(10–12), 1655–1666.
28.
MorrisS.WoodR. J. K.HarveyT. J.PowrieH. E. G.Electrostatic charge monitoring of unlubricated sliding wear of a bearing steel. Wear, 2003, 255, 430–443, 0043–1648.
29.
HearnG. L.Electrostatic ignition hazards arising from fuel flow in plastic pipes. J. Loss Prev. Proc. Ind., 2002, 15, 105–109.
30.
HarveyT. J.WoodR. J. K.PowrieH. E. G.WarrensC.Charging ability of pure hydrocarbons and lubricating oils. Tribol. Trans., 2004, 47(2), 263–271, 1040–2004.
31.
McGeehan, J. A. and Ryason, P. R. Preventing catastrophic camshaft lobe failures in low emission diesel engines. SAE paper 2000-01-2949, 2001.
32.
MuftiR. A.PriestM.Experimental and theoretical study of instantaneous engine valve train friction. J. Tribol., 2003, 125(3), 628–637.
33.
BellJ. C.Gasoline engine valve train design evolution and the antiwear requirements of motor oils. Proc. IMechE, Part J: J. Engineering Tribology, 1998, 212(4), 243–257.
34.
YamaguchiE. S.OnopchenkoA.FranciscoM. M.ChanC. Y.The relative oxidation inhibition performance of some neutral and basic zinc dithiophosphate salts. Tribol. Trans., 1999, 42(4), 895–901.
35.
Gee, M. G. Guidelines for unlubricated sliding wear tests, Parts 1 and 2. National Physical Laboratory, 1993.
36.
RoundsF. G.Generation of synthetic diesel engine oil soots for wear studies. Lubr. Eng., 1984, 40(7), 394–401.
37.
HosonumaK.YoshidaK.MatsunagaA.The decomposition products of zinc dialkyldithiophosphate in an engine and their interaction with diesel soot. Wear, 1985, 103(4), 297–309.
38.
BerbezierI.MartinJ. M.The adverse effect of carbon in mild wear with ZDDP lubricant additive. Tribol. Int., 1988, 21(2), 89–96.
39.
BerbezierI.MartinJ. M.KapsaP.Role of carbon in lubricated mild wear. Tribol. Int., 1986, 19(3), 115–122.
40.
KawamuraM.IshiguroT.FujitaK.MorimotoH.Deterioration of antiwear properties of diesel engine oils during use. Wear, 1988, 123(3), 269–280.
41.
Chinas-CastilloF.SpikesH. A.Behaviour of colloidal solid particles in elastohydrodynamic contacts. Tribol. Trans., 2000, 43(3), 387–394.
42.
GeorgeS.BallaS.GautamV.GautamM.Effect of diesel soot on lubricant oil viscosity. Tribol. Int., 2007, 40(5), 809–818.
43.
MortierR. M.OrszulikS. T.Chemistry and technology of lubricants, 1992, (Blackie Academic & Professional, UK).
44.
AdamenkoS. P.TsaregradskiiV. A.Change in properties of crankcase oil during engine operation on high-sulphur fuel. Chem. Technol. Fuels Oils, 1965, 1(9), 727–730.
45.
MasukoM.SuzukiA.UenoT.Influence of chemical and physical contaminants on the antiwear performance of model automotive engine oil. Proc. IMechE, Part J: J. Engineering Tribology, 2006, 220(5), 455–462.
46.
YamaguchiE. S.UntermannM.RobyS. H.RyasonP. R.YehS. W.Soot wear in diesel engines. Proc. IMechE, Part J: J. Engineering Tribology, 2006, 220(5), 463–469.
47.
KanetaM.IrieT.NishikawaH.MatsudaK.Effects of soot on wear in elastohydrodynamic lubrication contacts. Proc. IMechE, Part J: J. Engineering Tribology, 2006, 220(3), 307–317.
48.
GreenD. A.LewisR.Dwyer-JoyceR. S.Wear effects and mechanisms of soot-contaminated automotive lubricants. Proc. IMechE, Part J: J. Engineering Tribology, 2006, 220(3), 159–169.
49.
Chinas-CastilloF.SpikesH. A.The behaviour of diluted sooted oils in lubricated contacts. Tribol. Lett., 2004, 16(4), 317–322.
50.
ItahashiS.MitsuiH.SatoT.SoneM.State of water in hydrocarbon liquids and its effect on conductivity. IEEE Trans. Dielectr. Electr. Insulat., 1995, 2(6), 1117–1122.
51.
TaylorL. J.SpikesH. A.Friction enhancing properties of ZDDP antiwear additive. Part I – friction and morphology of ZDDP reaction films. Tribol. Trans., 2003, 46(3), 303–309.
52.
YamaguchiE. S.RyasonP. R.YehS. W.HansenT. P.Boundary film formation by ZnDTPs and detergents using ECR. Tribol. Trans., 1998, 41(2), 262–272.
53.
YahagiY.NagasawaY.HottaS.MitzutaniY.Corrosive wear of cast iron under reciprocating lubrication. SAE paper 861599, 1987.
TruhanJ. J.QuJ.BlauP. J.The effect of lubricating oil condition on the friction and wear of piston ring and cylinder liner materials in a reciprocating bench test. Wear, 2005, 259(7–12), 1048–1055.
56.
ColaciccoP.MazuyerD.The role of soot aggregation on the lubrication of diesel-engines. Tribol. Trans., 1995, 38(4), 959–965.
57.
YoshidaK.SakuraiT.Limitations of thin films in EHD contacts with dispersed phase systems as lubricants. Wear, 1994, 175(1–2), 71–79.
58.
StottF. H.MacDonaldA. G.The influence of acid strength on the corrosive wear of grey cast irons in oil-sulphuric acid mixtures. Wear, 1988, 122(3), 343–361.