Investigation of the role of tribolayer formation in improving drilling performance of Ti-6Al-4V using minimum quantity of lubrication

Abstract

Relationships between tribological properties of Ti-6Al-4V and the machining behaviour of the same alloy drilled by a WC-Co cutting tool using minimum quantity lubrication (MQL) were studied. The tribological behaviour of Ti-6Al-4V sliding against WC-Co was evaluated by determining the changes in the coefficient of friction (COF) using cutting fluids employed in MQL and flooded drilling tests. When pin-on-disk tests were carried out under the boundary lubricated condition, the MQL fluid (MQLF) provided a low COF of 0.16 at 25 ℃ and 0.24 at 250 ℃. The observed low COFs were attributed to formation of a tribolayer on the WC-Co counterfaces. A high COF of 0.45 observed at 300 ℃ indicated that the tribolayer was no longer stable. Application of conventional water-based cutting fluid (CF) also resulted in a low COF of 0.26 at 25 ℃ but the COF rose to 0.32 at 100 ℃. During drilling tests, MQLF was supplied at a rate of 80 ml/h using an external MQL system. The average drilling torque was reduced by 35% compared to CF as a result of the formation of tribolayer on the cutting edge of the tool as well as on the drilled hole surfaces, as the cutting temperature remained <250 ℃. According to Raman and X-ray photoelectron spectroscopy (XPS) analyses, the tribolayer on the drilled hole surface was formed as a result of degradation of additives in the MQL. The presence of phosphate- and sulfate-based anti-wear components in the tribolayer proved to be beneficial in preventing metal-metal contacts during drilling and provided a low COF. The low COF between tool-workpiece contact resulted in a low and uniform torque response throughout the drilling cycles and prevention of built-up edge (BUE) formation, leading to an improved surface finish.

Keywords

Tribolayer coefficient of friction boundary lubrication minimum quantity lubrication drilling Ti-6Al-4V WC-Co

Get full access to this article

View all access options for this article.

References

Masjuki

Maleque

. The effect of palm oil diesel fuel contaminated lubricant on sliding wear of cast irons against mild steel. Wear 1996; 198: 293–299.

Taylor

Spikes

. Friction-enhancing properties of ZDDP antiwear additive: Part I—friction and morphology of ZDDP reaction films. Tribol Transact 2003; 46: 303–309.

De Silva

Priest

Lee

, et al. Tribometer investigation of the frictional response of piston rings when lubricated with the separated phases of lubricant contaminated with the gasoline engine biofuel ethanol and water. Tribol Lett 2011; 43: 107–120.

Chen

Alpas

. Ultra-mild wear of a hypereutectic Al–18.5 wt.% Si alloy. Wear 2008; 265: 186–195.

Dey

Perry

Alpas

. Micromechanisms of low load wear in an Al–18.5% Si alloy. Wear 2009; 267: 515–524.

Chen

Meng-Burany

Perry

, et al. Micromechanisms and mechanics of ultra-mild wear in Al–Si alloys. Acta Materialia 2008; 56: 5605–5616.

Fujita

Spikes

. The formation of zinc dithiophosphate antiwear films. Proc IMechE, Part J: J Engineering Tribology 2004; 218: 265–278.

Spikes

. The history and mechanisms of ZDDP. Tribol Lett 2004; 17: 469–489.

Blau

Howe

, et al. Oxygen diffusion enables anti-wear boundary film formation on titanium surfaces in zinc-dialkyl-dithiophosphate (ZDDP)-containing lubricants. Scripta Materialia 2009; 60: 886–889.

10.

Bansal

Eryilmaz

Blau

. Surface engineering to improve the durability and lubricity of Ti–6Al–4V alloy. Wear 2011; 271: 2006–2015.

11.

Yang

Zhang

Dai

, et al. Tribological properties of titanium alloys under lubrication of SEE oil and aqueous solutions. Tribology Int 2017; 109: 40–47.

12.

Amanov

Sasaki

. A study on the tribological characteristics of duplex-treated Ti–6Al–4V alloy under oil-lubricated sliding conditions. Tribol Int 2013; 64: 155–163.

13.

Rahim

Sasahara

. A study of the effect of palm oil as MQL lubricant on high speed drilling of titanium alloys. Tribol Int 2011; 44: 309–317.

14.

Rahim E and Sasahara H. High speed MQL drilling of titanium alloy using synthetic ester and palm oil. In: Proceedings of the 36th international MATADOR conference, 14–16 July 2010, Manchester, Lancashire, United Kingdom, pp.193–196. MATADOR.

15.

Zeilmann

Weingaertner

. Analysis of temperature during drilling of Ti6Al4V with minimal quantity of lubricant. J Mater Process Technol 2006; 179: 124–127.

16.

Sadeghi

Haddad

Tawakoli

, et al. Minimal quantity lubrication-MQL in grinding of Ti–6Al–4V titanium alloy. Int J Adv Manuf Technol 2009; 44: 487–500.

17.

Sun

Wong

Rahman

, et al. Effects of coolant supply methods and cutting conditions on tool life in end milling titanium alloy. Mach Sci Technol 2006; 10: 355–370.

18.

Hassan A and Yao ZQ. Minimum lubrication milling of titanium alloys. Materials Science Forum 2004; 87–91.

19.

Rahim

Sasahara

. A study of the effect of palm oil as MQL lubricant on high speed drilling of titanium alloys. Tribol Int 2011; 44: 309–317.

20.

Rahim

Sasahara

. Investigation of tool wear and surface integrity on MQL machining of Ti-6AL-4V using biodegradable oil. Proc IMechE, Part B: J Engineering Manufacture 2011; 225: 1505–1511.

21.

Ibrahim

Haron

Ghani

. The effect of dry machining on surface integrity of titanium alloy Ti-6Al-4V ELI. J Appl Sci 2009; 9: 121–127.

22.

Bhowmick

Banerji

Alpas

. Tribological behavior and machining performance of non-hydrogenated diamond-like carbon coating tested against Ti–6Al–4V: effect of surface passivation by ethanol. Surface Coat Technol 2014; 260: 290–302.

23.

Gente

Hoffmeister

H-W

Evans

. Chip formation in machining Ti6Al4V at extremely high cutting speeds. CIRP Annals 2001; 50: 49–52.

24.

Fang

. A comparative study of the cutting forces in high speed machining of Ti–6Al–4V and Inconel 718 with a round cutting edge tool. J Mater Process Technol 2009; 209: 4385–4389.

25.

Sun

Guo

. A comprehensive experimental study on surface integrity by end milling Ti–6Al–4V. J Mater Process Technol 2009; 209: 4036–4042.

26.

Amin

Ismail

Khairusshima

. Effectiveness of uncoated WC–Co and PCD inserts in end milling of titanium alloy—Ti–6Al–4V. J Mater Process Technol 2007; 192: 147–158.

27.

Rahman

San WONG

Zareena

. Machinability of titanium alloys. JSME Int J Series C Mech Syst Mach Elements Manuf 2003; 46: 107–115.

28.

Nabhani

. Machining of aerospace titanium alloys. Robotics Comput-Integrated Manuf 2001; 17: 99–106.

29.

Bhowmick

Lukitsch

Alpas

. Dry and minimum quantity lubrication drilling of cast magnesium alloy (AM60). Int J Mach Tools Manuf 2010; 50: 444–457.

30.

Hutchings I and Shipway P. Tribology: friction and wear of engineering materials. Oxford, UK: Butterworth-Heinemann, 2017.

31.

Banerji

Lukitsch

Alpas

. Friction reduction mechanisms in cast iron sliding against DLC: Effect of biofuel (E85) diluted engine oil. Wear 2016; 368: 196–209.

32.

Bhowmick

Banerji

Alpas

. Tribological behavior of Al–6.5%,–12%,–18.5% Si alloys during machining using CVD diamond and DLC coated tools. Surface Coat Technol 2015; 284: 353–364.

33.

Dasch

Ang

Wong

, et al. A comparison of five categories of carbon-based tool coatings for dry drilling of aluminum. Surface Coat Technol 2006; 200: 2970–2977.

34.

Bhowmick

Alpas

. Minimum quantity lubrication drilling of aluminium–silicon alloys in water using diamond-like carbon coated drills. Int J Mach Tools Manuf 2008; 48: 1429–1443.

35.

Bhowmick

Alpas

. The performance of hydrogenated and non-hydrogenated diamond-like carbon tool coatings during the dry drilling of 319 Al. Int J Mach Tools Manuf 2008; 48: 802–814.

36.

Bhowmick

Alpas

. The performance of diamond-like carbon coated drills in thermally assisted drilling of Ti-6Al-4V. J Manuf Sci Eng 2013; 135: 061019.

37.

Rahman

Kumar

Salam

. Experimental evaluation on the effect of minimal quantities of lubricant in milling. Int J Mach Tools Manuf 2002; 42: 539–547.

38.

Trent EM and Wright PK. Metal cutting. Oxford, UK: Butterworth-Heinemann, 2000.

39.

Stepina V and Vesely V. Lubricants and special fluids. Amsterdam, the Netherlands: Elsevier, 1992.

40.

Crobu

Rossi

Mangolini

, et al. Chain-length-identification strategy in zinc polyphosphate glasses by means of XPS and ToF-SIMS. Analytical Bioanalytical Chem 2012; 403: 1415–1432.

41.

Varlot

Martin

Grossiord

, et al. A dual-analysis approach in tribochemistry: application to ZDDP/calcium borate additive interactions. Tribol Lett 1999; 6: 181–189.

42.

Chen

Bosse

Deters

. Effects of various base oils and additives on the tribological behaviour of lubricated aluminium-on-aluminium and steel-on-aluminium contacts. Proc IMechE, Part J: J Engineering Tribology 2009; 223: 571–580.

43.

Chusuei

Goodman

Van Stipdonk

, et al. Calcium phosphate phase identification using XPS and time-of-flight cluster SIMS. Analytical Chem 1999; 71: 149–153.

44.

Bhowmick

Sun

Alpas

. Low friction behaviour of boron carbide coatings (B4C) sliding against Ti–6Al–4V. Surface Coat Technol 2016; 308: 316–327.