Delamination failure of composite top-hat stiffeners using finite element analysis

Abstract

The paper presents the finite element analysis of top-hat stiffeners (transversely loaded keel support structure) under a static load where splitting–delamination is the primary mode of failure. A set of experiments is conducted on the composite top-hat stiffeners with three different lay-up arrangements. The experimental study, together with the finite element modelling to capture the delamination failure, is presented. Fracture initiation is predicted using an interlaminar-strength-based criterion. A fracture-mechanics-based formulation is used to predict delamination propagation by connecting the composite layers with two-dimensional and three-dimensional interface elements using the commercially available MSC Marc Mentat 2008 r1 finite element software package. Reasonable agreement between the experiments and finite element analysis was achieved. The reserve strength identified by the experimental testing is successfully modelled. The factors affecting the fibre–matrix interface strength are studied. The failure location and mode for fracture initiation and propagation are determined.

Keywords

Composites top-hat stiffener delamination interlaminar failure reserve strength

Get full access to this article

View all access options for this article.

References

Mouritz

Leong

Herszberg

A review of the effect of stitching on the in-plane mechanical properties of fibre-reinforced polymer composites. Composites Part A: Appl Sci Mfg 1997; 28: 979–991.

Mouritz

Gallagher

Goodwin

. Flexural strength and interlaminar shear strength of stitched GRP laminates following repeated impact. Composites Sci Technol 1997; 87: 509–522.

Sridharan

. Delamination behaviour of composites. Boca Raton, FL: CRC Press, 2008.

Kedward

Wilson

McLean

. Flexure of simply curved composite shapes. Composites 1989; 20(6): 527–536.

Graff

. Mechanical behaviour of thick, curved laminated composites. PhD Thesis, Stanford University, Stanford, CA, USA, 1989.

Martin

Jackson

. Damage prediction in cross-plied curved composite laminates. Composite Mater, Fatigue Fracture 1993; 4: 105–126.

Dodkins

Shenoi

Hawkins

. Design of joints and attachments in FRP ship structures. Mar Structs 1994; 7: 364–398.

Wisnom

. 3-D finite element analysis of curved beams in bending. J Composite Mater 1996; 30(11): 1178–1190.

Kaczmarek

Wisnom

Jones

. Edge delamination in curved (0₄/+/–45₆)_s glass-fibre/epoxy beams loaded in bending. Composite Sci Technol 1998; 58: 155–161.

10.

Lekhnitskii

. Anisotropic plates. New York: Gordon and Breach, 1968.

11.

Shenoi

Wang

. Through-thickness stresses in curved composite laminates and sandwich beams. Composites Sci Technol 2001; 61: 1501–1512.

12.

Prusty

Ray

Satsang

. Progressive failure analysis of laminated unstiffened and stiffened composite panels. J Reinf Plastics Composites 2005; 24(6): 633–642.

13.

Prusty

. Linear static analysis of composite hat-stiffened laminated shells using finite elements. Finite Elements Analysis Des 2003; 39: 1125–1138.

14.

Raju Prusty

Kelly

. Top hat stiffeners: a study on keel failures. Ocean Engng 2010; 37(13): 1180–1192.

15.

Shenoi

Hawkins

. An investigation into the performance characteristics of top-hat stiffener to shell plating joints. Composite Structs 1995; 30: 109–121.

16.

Pei

Shenoi

. Examination of key aspects defining the performance characteristics of out-of-plane joints in FRP marine structures. Composites Part A: Appl Sci Mfg 1996; 27: 89–103.

17.

Phillips

Shenoi

Moss

. Damage mechanics of top-hat stiffeners used in FRP ship construction. Mar Structs 1999; 12: 1–19.

18.

Eksik

Shenoi

Blake

JIR

Jeong

. Damage mechanisms of hat-shaped GRP beams. J Reinf Plastics Composites 2004; 23(14): 1497–1514.

19.

Eksik

Shenoi

Moy

Jeong

. Finite element analysis of top-hat-stiffened panels of fiber-reinforced-plastic boat structures. Mar Technol 2007; 44(1): 16–26.

20.

Choi

Chang

. A new approach toward understanding damage mechanisms and mechanics of laminated composites due to low-velocity impact: Part II – analysis. J Composite Mater 1991; 25: 1012–1038.

21.

. Role of matrix resin in delamination onset and growth in composite laminates. Composites Sci Technol 1988; 33(4): 257–277.

22.

Pearce

. High strain rate behaviour of bolted joints in carbon fibre composite structures. PhD Thesis, University of New South Wales, Sydney, Australia, 2010.

23.

Griffith

. The phenomena of rupture and flow in solids. Phil Trans R Soc London A 1921; 221: 163–198.

24.

Irwin

. Fracture dynamics. In: ASM symposium on fracturing of metals, Chicago, IL, USA, June 1947, Trans Am Soc Metals 1948; 40A: 147–166.

25.

Irwin

. Fracture. Handb Physik 1958; 6: 558–590.

26.

Irwin

. Analysis of stresses and strains near the end of a crack transversing a plate. J Appl Mech 1957; 24: 361–364.

27.

Rybicky

Kanninen

. A finite element calculation of stress intensity factors by a modified crack closure integral. Engng Fracture Mech 1977; 9(4): 931–938.

28.

Orifici

Thomson

Degenhardt

. Development of a finite-element analysis methodology for the propagation of delaminations in composite structures. Mech Composite Mater 2007; 43(1): 9–28.

29.

Cui

Wisnom

. A combined stress-based and fracture-mechanics-based model for predicting delamination in composites. Composites 1993; 24(6): 467–474.

30.

Lammerant

Verpoest

. Modelling of the interaction between matrix cracks and delaminations during impact of composite plates. Composites Sci Technol 1996; 56: 1171–1178.

31.

Goyal

Jaunky

Johnson

Ambur

. Intralaminar and interlaminar progressive failure analyses of composite panels with circular cut-outs. Composite Structs 2004; 64(1): 91–105.

32.

Petrossian

Wisnom

. Prediction of delamination initiation and growth from discontinuous plies using interface elements. Composites Part A: Appl Sci Mfg 1998; 29(5–6): 503–515.

33.

de Moura

MFSF

Goncalves

JPM

Marques

de Castro

PMST

. Prediction of compressive strength of carbon-epoxy laminates containing delamination by using a mixed-mode damage model. Composite Structs 2000; 50: 151–157.

34.

Turon

Dávila

Camanho

Costa

. An engineering solution for mesh size effects in the simulation of delamination using cohesive zone models. Engng Fracture Mech 2007; 74: 1665–1682.

35.

Marc® 2008r1 – Vol A: Theory and User Information. Santa Ana, CA: MSC Software 2008.

36.

Hou

Petrinic

Ruiz

. A delamination criterion for laminated composites under low-velocity impact. Composite Sci Technol 2001; 61: 2069–2074.

37.

Mouritz

Baini

Herszberg

. Mode I interlaminar fracture toughness properties of advanced textile fibreglass composites. Composites Part A: Appl Sci Mfg 1999; 30: 859–870.

38.

Johnson

. Comparison of the mechanical properties of SMC with laminated GRP materials. Composites 1986; 3: 233–239.

39.

Dirand

Hilaire

Soulier

Nardin

. Interfacial shear strength in glass-fiber/vinylester-resin composites. Composites Sci Technol 1996; 56: 533–539.

40.

Perrot

Baley

Grohens

Davies

. Damage resistance of composites based on glass fibre reinforced low styrene emission resins for marine applications. Appl Composite Mater 2007; 14: 67–87.

41.

Park

Jang

. Effect of surface treatment on the mechanical properties of glass fiber/vinylester composites. J Appl Polym Sci 2004; 91: 3730–3736.

42.

Kitching

Tau

Abu-Mansour

TMN

. The influence of through thickness properties on glass reinforced plastic laminated structures. Composite Structs 1984; 2: 105–151.