Adsorption and desorption properties of modified feather and feather/polypropylene melt-blown filter cartridge of lead ion (Pb 2+ )

Abstract

Duck and chicken feather fibers are waste products of the poultry industry, creating a serious solid waste problem around the world. Previous works showed that feather fibers can be reused to adsorb heavy metal ions from water. But the raw feather fiber only exhibits moderate heavy metal ions adsorption capacity, not cost-effective to be reused as adsorbent in a large scale. To improve the adsorption capacity of feather fibers, sodium pyrosulfite (Na₂S₂O₅) was used in this paper to modify the feather fiber in order to improve its Pb²⁺ adsorption capacity. Scanning electron microscopy and Fourier transform infrared spectroscopy quantified chemical and structural changes of Na₂S₂O₅-modified feather fibers. In addition, Na₂S₂O₅-modified feather fibers were processed into feather/polypropylene melt-blown filter cartridges and their dynamic Pb²⁺ adsorption properties were investigated by using the test equipment set up in our lab. Finally, the desorption effects of NaOH and sodium sulfide nonahydrate (Na₂S·9H₂O) aqueous solutions on the feather fiber adsorbed with Pb²⁺ were studied. It is found that Pb²⁺ adsorption capacity of the feather fiber increased after being modified by Na₂S₂O₅. Modified feather/polypropylene filter cartridge exhibited higher Pb²⁺ adsorption capacity than feather/polypropylene filter cartridge and pure polypropylene filter cartridge in the whole dynamic adsorption process.

Keywords

Feather adsorption desorption melt-blown filter cartridge

Introduction

The wastewater generated from many industries, such as tanning, battery, glassware, ceramics, electroplating, mining, paints and photographic industry, contains a number of heavy metal ions like chromium, lead, cadmium, etc. which have significant toxic effects and these pollutants requires removal before discharge into the main stream [1]. Nowadays people have realized that heavy metal ions remaining in the drinking water are harmful and toxic to human health. Long-term drinking of Pb²⁺ ion-containing water, even at very low concentrations, could lead to a broad spectrum of health problems, including nausea, convulsions, coma, renal failure, cancer and subtle effects on metabolism and intelligence [2].

Different approaches to remove Pb²⁺ ions from wastewaters, including chemical precipitation, ion exchange, reverse osmosis and adsorption, have been reported. Among them, adsorption is one of the most important methods because of its easy operation and versatility [3]. Various adsorbents have been explored to remove heavy metal ions from wastewaters. Biosorption material, a kind of low-cost adsorbent with excellent sorption capacity, is gaining more and more attention. Peat, sugar cane bagasse, eucalyptus bark and hen feather have been implemented for the removal of specific metals from wastewaters [4,5]. However, the feasibility of biosorption versus traditional methods has been questioned on the basis of a series of limitations: the relatively low metal uptake, the high brittleness of the biomass and the inherent poor reproducibility. Compared to other biomass sorbents, the feather fiber comprises excellent mechanical properties, resists hydrolytic degradation and is durable. It is said that the feather fiber is constituted with four parts from outside to inward, which are named as epicuticle film, cuticle layer, skin layer and cortex, of which the epicuticle film is a layer of biologic cell membrane with thickness approximately 0.02–0.10 µm. The biologic cell membrane is mainly made of sterol and bimolecular layers of triphosphate ester, and these chemicals are responsible for the excellent water repellant properties of feather fibers [6]. But as a biomass sorbent, the hydrophobic properties of the feather fiber are a serious drawback in the processing of aqueous metal ion solutions. The raw feather fiber only exhibits moderate heavy metal ions absorption capacity, not cost-effective to be reused as adsorbent in a large scale.

Recently, much research has focused on the sorption properties of feather fibers as sorbents for the removal of heavy metals, phenol and organic dyes from their aqueous solutions [7 –11]. Banat et al. compared the sorption capacities of some keratin-based compounds, including the feather fiber, for the removal of Zn²⁺ ions from aqueous solutions in a batch configuration and using different conditions of pH and temperature [12]. The research on Zn²⁺ adsorption properties of feather fiber before and chemical treatment showed that the feather fiber treated with alkaline aqueous solutions absorbed more metal ions than those treated with an anionic surfactant and untreated feather fiber [13]. Many research works have been carried by chemical grafting, alkaline treatment, powdering, dissolution, etc. to improve the adsorption capacity of the feather fiber [14]. Keratin mainly comprises amino and carboxyl groups, has a good biocompatibility, nontoxic and skin-friendly properties present in wool and feather fiber. These fibers are generally used to extract keratin. Reduction is the main method of dissolving wool, where the disulfide bonds of keratin are cleaved [15]. Sodium pyrosulfite (Na₂S₂O₅) aqueous solution, one of the important reducing reagents, is widely used to dissolve wool or remove the scale of wool. Wang and Liu [16] inferred that it can be used to modify the feather fiber for improving its Pb²⁺ adsorption capacity.

In another study, Kar and Misra reported the removal of Zn²⁺ using the feather fiber in a multicomponent aqueous solution of Cu²⁺, Pb²⁺, Zn²⁺, Cd²⁺ and Ni²⁺ at different pH values [17]. Most of the above-mentioned studies on the removal of Zn²⁺ ions using the feather fiber have been focused on sorption experiments using batch configurations. Aguayo-Villarreal et al. first studied the batch and column Zn²⁺ removal from aqueous solution using chicken feather fibers as sorbents [18]. Duck feather was processed into a kind of composite made from nonwoven fabric with bicomponent fiber, which showed good mechanical properties and absorption capacities of Cu²⁺ and Cr⁶⁺ bicomponent aqueous solution [14]. As we know, melt-blown filter cartridge is widely used nowadays to clean water, filtering out insoluble impurities. It is significant to endow it with heavy metal ions adsorption property at the same time. In this paper, feather/polypropylene (PP) melt-blown filter cartridges were prepared and their dynamic Pb²⁺ adsorption properties were investigated as well.

In addition, recovering the metal biosorbed or reusing the biomass is one of the essential issues to scale up biosorption technology. This work will examine the effects of sodium hydroxide (NaOH) and sodium sulfide nonahydrate (Na₂S·9H₂O) as eluents to regenerate the feather fiber adsorbed with Pb²⁺.

Experimental

Materials

The duck feather fiber without scapus was supplied by Yangzhou Ganquan Down Products Factory. PP with melt flow index 35 was purchased from Sinopec Shanghai Petrochemical Company Ltd. Lead nitrate (Pb(NO₃)₂) was used to prepare Pb²⁺ solution. NaOH and Na₂S·9H₂O were used as desorption reagents. Na₂S₂O₅ and urea were used to modify feather fibers. Nitric acid (HNO₃) was used in the inductively coupled plasma atomic emission spectrometry (ICP-AES) measurement. Ammonia aqueous solution (NH₃·H₂O) was used to adjust the pH value of solutions. All chemicals are all analytical grade.

Modification of the feather fiber

A total of 1, 3, 5, 10 and 15 g Na₂S₂O₅ were added into 200 ml de-ionized water under 65℃, respectively. Twenty grams of urea was added to every solution as well. Ten grams of feather fiber was put into the above solutions, respectively. The solutions were stirred for 5 min and then were allowed to stand for 2 h. Finally, the solutions were filtered and feather fibers were washed thoroughly with de-ionized water and air-dried at room temperature for further use.

Preparation of feather/PP melt-blown filter cartridges

Feather/PP melt-blown filter cartridges were made by fixing an extra feather fiber feeding unit on a traditional melt-blown nonwoven production machine, as shown in Figure 1. The feather fiber was blown out by a fan uniformly from the unit and mixed with PP melt-blown nonwoven fibers spun from the spinneret of the melt-blown equipment and reached a pivot with a core, which rotated and moved back and forth to form the cylindrical shape of a filter cartridge. In this paper, three kinds of filter cartridges were made, i.e. feather/PP melt-blown filter cartridge, modified feather/PP melt-blown filter cartridge and pure PP melt-blown filter cartridge. Their structural properties were listed in Table 1. Photo of the feather /PP melt-blown filter cartridge was shown in Figure 2. Feather/PP and modified feather/PP melt-blown filter cartridges are constituted with multilayers. The inner layer is composed of pure PP melt-blown nonwoven fibers, the middle layer is composed of the feather fiber and PP melt-blown nonwoven fiber in a ratio listed in Table 1 and the outer layer is composed of pure PP melt-blown nonwoven fibers to endow the whole filter cartridge with high physical and mechanical properties. The inside diameter of the cartridge is 30 mm and the length of the cartridge is 250 mm.

Table 1.

Properties of feather/PP melt-blown filter cartridges.

Samples	Feather/PP	Modified feather/PP	PP
Weight of filter cartridge (g)	164	163	158
Content of feather fibers (%)^a	48.8	49.1	0
Outer diameter (mm)	64	64	66

Content of feather fibers is the ratio of the weight of feather fibers to the weight of the filter cartridge expressed as a fraction of 100.

Adsorption experiment of the feather fiber

Two grams of duck feather fiber was immersed in 250 ml Pb(NO₃)₂ aqueous solution containing 100 mg/l Pb²⁺ under 25℃. The solution was stirred for 5 min and then was allowed to stand for 1 h. Finally, the solution was filtered and the residual Pb²⁺ concentration of the filtrate was measured by using ICP-AES. The Pb²⁺ adsorption capacity of the feather fiber is calculated according to equation (1)

Q_{1} = \frac{(C_{0} - C_{1}) \times V_{1}}{M_{1}}

(1)

where Q₁ is Pb²⁺ adsorption capacity of the feather fiber (mg/g), C₀ is the initial Pb²⁺ concentration of Pb(NO₃)₂ aqueous solution (mol/l), C₁ is the residual Pb²⁺ concentration in Pb(NO₃)₂ aqueous solution after adsorption (mol/l), V₁ is the volume of Pb(NO₃)₂ aqueous solution (l) and M₁ is the weight of the feather fiber before adsorption (g).

Dynamic Pb²⁺ adsorption measurement of filter cartridges

Most studies on the removal of heavy metal ions using the feather fiber have been focused on sorption experiments using batch configurations. In this paper, melt-blown filter cartridge was prepared and dynamic Pb²⁺ adsorption test equipment was set up by us. The melt-blown filter cartridge was fixed by hot melt adhesive on both ends with two end caps, one of which has hole in the center as shown in Figure 3(b). The end of the cartridge with hole was inserted into the support post of the filter cartridge vessel, as shown in Figure 3(c).

Dynamic Pb²⁺ adsorption equipment was set up in our lab as shown in Figure 4, which is constituted with pressure gauge, flow meter, filter cartridge and pump. Pb(NO₃)₂ aqueous solution with concentration of about 0.3 mol/l was sucked from the reservoir by the pump. It flowed through the valve, pressure gauge 1 and flow meter 1, and then went into the filter cartridge from the outer layer into the inner layer and then flowed out from the hole under the filter cartridge. The solution went through pressure gauge 2 and flow meter 2 and went back to the reservoir, and then repeated in this way. A small amount of the solution was taken from the reservoir every 30 min and Pb²⁺ concentration was measured by using ICP-AES.

Desorption experiment

Duck feather fibers adsorbed with Pb²⁺ from the above Pb²⁺ adsorption experiment were washed thoroughly with de-ionized water and air-dried at room temperature. Then they were immersed in NaOH and Na₂S·9H₂O aqueous solutions with different concentration under 40℃ for 1 h, respectively. Finally, the solutions were filtered and Pb²⁺ concentration of the residual solutions was measured by using ICP-AES. The desorption capacity of the feather fiber under different solutions is calculated according to equation (2)

Q_{2} = \frac{C_{2} \times V_{2}}{M_{2}}

(2)

where Q₂ is the desorption capacity of the feather fiber (mg/g), C₂ is Pb²⁺ concentration of the desorption solution (mol/l), V₂ is the volume of the desorption solution (l) and M₂ is the weight of the feather fiber used in the experiment (g).

Duck feather fiber after NaOH desorption experiment was used to absorb Pb²⁺ according to the above procedure of adsorption experiment. Its Pb²⁺ absorption capacity was measured by the same method. The adsorption and desorption experiment was repeated for 12 times.

Measurement

ICP-AES

ICP-AES was used to measure Pb²⁺ concentration in the solution. Five per cent HNO₃ was used as the media.

Scanning electronic microscopy (SEM)

Surface of feather fibers before and after Na₂S₂O₅ modification was observed by using Japan JSM-5600LV SEM. The surface of samples was spurred with gold and observed under 10 kV.

Fourier transform infrared (FTIR) spectroscopy analysis

Duck feather fiber was mixed and grounded with KBr and made into a pellet. Then it was tested with Nicollet NEXUS670 infrared-Raman spectroscopy tester. The wavenumber was 500–4000 cm⁻¹, the resolution was 8 cm⁻¹ and the scan number was 64.

Results and discussion

Influences of Na₂S₂O₅ treatment on Pb²⁺ adsorption of the feather fiber

Urea is a kind of protein denaturant. It is often used together with Na₂S₂O₅ to modify protein [19]. In this paper, the feather fiber was treated by Na₂S₂O₅ under different concentrations, while the concentration of urea remained unchanged. The Pb²⁺ adsorption capacity of modified feather fibers was shown in Figure 5.

It can be seen from Figure 5 that Pb²⁺ adsorption capacity of the feather fiber increased with increase in the concentration of Na₂S₂O₅ aqueous solution and reached the highest value when the concentration of Na₂S₂O₅ aqueous solution was 0.079 mol/l. The Pb²⁺ adsorption capacity of raw feather fiber was 6.11 mg/g, while the highest Pb²⁺ adsorption capacity of modified feather fiber was 11.16 mg/g, over 80% higher than that of the raw feather fiber. Then the Pb²⁺ adsorption capacity of the feather fiber decreased a little and kept unchanged with the increase of Na₂S₂O₅ aqueous solution concentration.

Structural changes of the feather fiber before and after Na₂S₂O₅ modification

In order to uncover the reason why Pb²⁺ adsorption capacity of the feather fiber was improved after Na₂S₂O₅ modification, surface structure and secondary morphology of the feather fiber before and after Na₂S₂O₅ modification were investigated by SEM and FTIR and the results were shown in Figures 6 to 8, respectively.

It can be seen from Figure 6 that the sub-branch of the feather fiber carried a number of fibrils, which showed knars or pinaculums around the surface. Rough grooves appeared on the surface of the sub-branches of the feather fiber. After Na₂S₂O₅ modification, the surface of sub-branches of the feather fiber became smooth and the feather fiber became slimmer. It is hypothesized that keratin fragments scaled off from the feather fiber surface layer by layer when it was treated by Na₂S₂O₅ aqueous solution, which was also observed by Sun when the feather fiber was treated by NaOH solution [20].

The two primary bands of IR spectra of proteins are 1600–1700 cm⁻¹ for amide I and 1500–1560 cm⁻¹ for amide II, which arise from specific stretching and bending vibrations of the protein backbone [21,22]. All of the secondary structures of proteins (α-helix, β-sheet and random coil) have characteristic bands at amide I and amide II. For chicken feather fiber protein, the amide I and amide II bands appear at around 1640 and 1530 cm⁻¹, respectively [7,20,23]. It can be seen from Figure 8 that the two spectra were identical to each other and the characteristic bands of α-helix and β-sheet secondary structures of the duck feather fiber before and after Na₂S₂O₅ modification were all observed 1630 and 1540 cm⁻¹ in FTIR spectra, respectively. As we know, the band at 1450 cm⁻¹ is the characteristic band of the main chain of feather fibers and can be used as the benchmark to relatively compare the band intensity of α-helix and β-sheet structure. Hence, the band intensity of 1450 cm⁻¹ is fixed to the same for all the samples, then the band intensity of α-helix is subtracted from the band intensity of β-sheet, and the differences are listed in Table 2.

Table 2.

Difference in peak intensity of α and β structures of modified feather fibers.

	Y₁₆₃₀	Y₁₅₄₀	Y_β–Y_α
Raw feather fiber	42.3	66.8	24.5
Na₂S₂O₅-modified feather fiber	67.9	94.7	26.8

Y₁₆₃₀ and Y₁₅₄₀ represent the infrared transmittance of the bands at 1630 and 1540 cm⁻¹, respectively.

It can be found from Table 2 that the difference in the band intensity of the two characteristic bands became more noticeable for the feather fiber after Na₂S₂O₅ modification. In other words, it seems that more α-helix structure appeared after the feather fiber was modified by Na₂S₂O₅. Compared to β-sheet, α-helix is more loose structure of the feather proteins, in which more hydrogen and/or disulfide bonds of feather keratin were broken during Na₂S₂O₅ modification. Hence more adsorptive sites are available for Pb²⁺ and the adsorption capacity of the feather fiber was improved after Na₂S₂O₅ treatment.

In addition, it is reported that the bands at 1079 and 1117 cm⁻¹ arise from specific stretching and bending vibrations of S–O bond of cysteine, resulting from the broken disulfide bond of cysteine [22]. However, the spectra of feather fibers with and without Na₂S₂O₅ modification were identical in the frequency range, suggesting that Na₂S₂O₅ modification did not change the chemical structure of feather fibers to a detectable extent by FTIR spectroscopy. Perhaps Na₂S₂O₅ modification only changed hydrogen bonds of feather keratin. More hydrogen bonds of feather keratin were broken with the increase in the concentration of Na₂S₂O₅ aqueous solution. However, only a fraction of hydrogen bonds of feather keratin can be broken by Na₂S₂O₅ aqueous solutions because of the constraint of disulfide bond. Hence it can be found from Figure 5 that Pb²⁺ adsorption capacity of the feather fiber increased with increase in the concentration of Na₂S₂O₅ aqueous solution and reached the highest value when the concentration of Na₂S₂O₅ aqueous solution was 0.079 mol/l.

Desorption effects of Na₂S·9H₂O and NaOH solutions on the feather fiber

One of the advantages of the adsorption method is that the absorbent can be regenerated and used repeatedly. In other words, the absorbent should be desorbed. The desorption process for the recovery of metals is based on several mechanisms. Basically, there are three desorption mechanisms [24]: (i) Precipitation of the metal adsorbed by formation of insoluble compounds with the desorbent agent, e.g. H₂S. (ii) Complexation of the metal adsorbed by reaction with compounds which have pairs of electrons available to share with the metal cation. Desorbent agents such as EDTA follow this mechanism. (iii) Ion exchange. Among them, ion-exchange method gives good yields by exchanging a cation from the desorbent reagent for the metal adsorbed. It is not convenient and safe to prepare H₂S in the lab. In this paper, Na₂S·9H₂O [25] and NaOH [26] were used as desorption reagent for feather fibers and their desorption of Pb²⁺ ions from feather fibers is shown in Table 3.

Table 3.

Desorption properties of NaOH and Na₂S·9H₂O solutions on feather fibers.

Concentration of desorbents (mol/l)	0.01	0.02	0.03	0.05
Desorption capacity of NaOH (mg/g)	1.46	1.58	1.89	1.86
Desorption capacity of Na₂S·9H₂O (mg/g)	0.02	0.04	0.08	–

It can be seen from Table 3 that Na₂S·9H₂O showed quite low Pb²⁺ desorption capacity and its desorption effect did not change obviously with the increase of the concentration of desorbent solutions. Only about 1.3% Pb²⁺ of the feather fiber was desorbed by Na₂S·9H₂O. The desorption capacity of NaOH is 24–31% of the adsorption capacity of raw feather fibers, which is 6.11 mg/g as shown in Figure 5. It is hypothesized that Pb(OH)₂ and PbS would form, when the Pb2 + adsorbed-feather fiber was immersed in NaOH and Na₂S·9H₂O aqueous solution, respectively. The solubility product constant of Pb(OH)₂ is 1.43 × 10⁻²⁰, which is much higher than that of PbS (3.4 × 10⁻²⁸). Hence more PbS deposit should be formed. However, it was found that the feather fiber changed color obviously and became nearly broken up when the concentration of Na₂S·9H₂O aqueous solution was as high as 0.03 mol/l, suggesting that Na₂S·9H₂O preferentially involved in the reaction with keratin of the feather fiber rather than with Pb²⁺ ion. Hence NaOH showed better desorption effect than Na₂S·9H₂O. In addition, the desorption capacity of NaOH did not change obviously when its concentration was increased to 0.05 mol/l. It is reported that complex ions, such as [Pb(OH)₄]²⁻, Pb₄(OH)₄⁴⁺, Pb₃(OH)₄²⁺ and Pb₆O(OH)₆⁴⁺ will be formed when the pH value is higher than 9. Pb(OH)₂ deposit will be re-dissolved correspondingly.

In order to further investigate the desorption effect of NaOH, duck feather fibers were treated by adsorption and desorption experiment for 12 times. The Pb²⁺ absorption capacity of feather fibers after each desorption cycle was shown in Figure 9.

It can be found from Figure 9 that Pb²⁺ absorption capacity of the NaOH-treated feather fibers increased with the increase of the desorption cycles, suggesting that NaOH is an available desorbent reagent to reuse feather fibers as an Pb²⁺ absorbent.

Dynamic Pb²⁺adsorption properties of feather/PP melt-blown filter cartridges

In this paper, the feather fibers with and without Na₂S₂O₅ modification were made into feather/PP and modified feather/PP melt-blown filter cartridge according to the patent titled a kind of feather/PP composite melt-blown filter cartridge and its process [27]. It is found that the feather fiber could be easily bonded to each other by PP melt-blown nonwoven fibers and the filter cartridges had good physical and mechanical properties. In addition, the dynamic Pb²⁺ adsorption properties of the three kinds of filter cartridges as listed in Table 1 were measured by using the test equipment set up in our lab as shown in Figure 10.

It is found from Figure 10 that modified feather/PP filter cartridge had higher Pb²⁺ adsorption capacity than feather/PP filter cartridge and pure PP filter cartridge in the whole dynamic adsorption process measured in this paper. In addition, the Pb²⁺ adsorption capacity of pure PP filter cartridge was a little lower than that of feather/PP filter cartridge. As shown above, the Pb²⁺ uptake capacity of raw feather fibers is about 6.11 mg/g. It is reported that the Pb²⁺ adsorption capacity of PP strip is about 0.1 mg/g [28], which is much lower than that of feather fibers. It is believed that PP fibers of these two kinds of filter cartridges have higher specific surface area, resulting in higher Pb²⁺ uptake capacity than that of PP strip. When modified feather/PP filter cartridge was used as the filter cartridge, Pb²⁺ concentration in the solution decreased faster in the first hour in comparison with the other two filter cartridges, suggesting that modified feather/PP filter cartridge had faster Pb²⁺ adsorption speed in the initial dynamic Pb²⁺ adsorption process. In the third hour of the dynamic adsorption process, the residual Pb²⁺ in the solution was about 0.09 mol/l. Based on the assumption that melt-blown filter cartridge is widely used as liquid filtration material, modified feather/PP melt-blown filter cartridge is a promising material, exhibiting filtration and Pb²⁺ adsorption functions at the same time.

Conclusion

In this paper, Na₂S₂O₅ was first used to modify the feather fiber in order to improve its Pb²⁺ adsorption capacity. SEM and FTIR were used to investigate the structural changes of the feather fiber before and after modification. In addition, the desorption effects of NaOH and Na₂S·9H₂O aqueous solutions on the feather fiber were studied. Finally, feather fibers were processed into feather/PP melt-blown filter cartridges and their dynamic Pb²⁺ adsorption properties were investigated by using the test equipment set up in our lab. First, it is concluded that Pb²⁺ adsorption capacity of the feather fiber increases after being modified by Na₂S₂O₅. The highest Pb²⁺ adsorption capacity of the modified feather fiber is over 80% higher than that of the raw feather fiber. Second, NaOH is an effective desorbent agent for the Pb²⁺ loaded feather fibers; Third, Na₂S·9H₂O did not show expected Pb²⁺ desorption effect. It involved in the reaction with feather keratin rather than with Pb²⁺ during the desorption experiment. Finally, modified feather/PP filter cartridge has higher Pb²⁺ adsorption capacity than feather/PP filter cartridge and pure PP filter cartridge in the whole dynamic adsorption process.

Na₂S₂O₅-treated feather/PP melt-blown filter cartridge is a kind of promising material for wastewater effluent treatment. For example, it can be used to remove Pb²⁺ existing in the wastewater yielded in the course of mechanical crushing and hydraulic sorting for waste lead acid batteries recycling. Compared to other processes, the filter cartridge can filter the insoluble particles in the wastewaters while keeping the Pb²⁺ adsorption property. In addition, feather fibers are waste products of the poultry industry. Na₂S₂O₅-treated feather/PP melt-blown filter cartridge can be prepared easily by modified commercial melt-blown equipment. But more work should be done to test the long-term filtration performance and the desorption properties of the Na₂S₂O₅-treated feather/PP melt-blown filter cartridge prepared in this paper.

Footnotes

Declaration of Conflicting Interests

The author(s) declared no potential conflicts of interest with respect to the research, authorship, and/or publication of this article.

Funding

The author(s) disclosed receipt of the following financial support for the research, authorship, and/or publication of this article:

The authors gratefully acknowledge the financial support from the Shanghai Municipal Natural Science Foundation (11ZR1400900) and Shanghai University Students’ Innovative Entrepreneurship Training Project ‘research and development of waste feather fiber melt-blown filter cartridge’.

References

Gupta

Carrott

PJM

Ribeiro Carrott

MML

. Low-cost adsorbents: Growing approach to wastewater treatment—a review. Crit Rev Environ Sci Technol 2009; 39: 783–842.

Rashed

. Lead removal from contaminated water using mineral adsorbents. Environmentalist 2001; 21: 187–195.

Lezcano

González

Ballester

. Sorption and desorption of Cd, Cu and Pb using biomass from a eutrophized habitat in monometallic and bimetallic systems. J Environ Manage 2011; 92: 2666–2674.

Wang

Jin

. Cu²⁺ Uptake mechanism of feather fiber. J Donghua Univ 2011; 6: 743–747.

Laus

Costa

Szpoganicz

. Adsorption and desorption of Cu(II) and Pb(II) ions using chitosan crosslinked with epichlorohydrin-triphosphate as the adsorbent. J Hazard Mater 2010; 183: 233–241.

Gao

Pan

. Structures and properties of the goose down as a material for thermal insulation. Text Res J 2007; 8: 617–626.

Sun

Liu

. Particles from bird feather: A novel application of an ionic liquid and waste resource. J Hazard Mater 2009; 170: 786–790.

De la Rosa

Reynel-Avila

Bonilla-Petriciolet

. Recycling poultry feathers for Pb removal from wastewater: Kinetic and equilibrium studies. Int J Chem Biomol Eng 2008; 1: 185–193.

Kyozo

. Biosorption of precious metal ions by chicken feather. J Appl Biochem Biotechnol 1996; 57–58: 67–74.

10.

Al-Asheh

Banat

Al-Rousan

. Adsorption of copper, zinc and nickel ions from single and binary metal ion mixtures on to chicken feathers. Adsorpt Sci Technol 2002; 20: 849–864. .

11.

Banat

Al-Asheh

. Biosorption of phenol by chicken feather. Environ Eng Policy 2000; 1: 85–90.

12.

Banat

Al-Asheh

Al-Rousan

. Comparison between different keratin composed biosorbents for the removal of heavy metal ions from aqueous solutions. Adsorpt Sci Technol 2002; 20: 393–416.

13.

Al-Asheh

Banat

Al-Rousan

. Beneficial use of chicken feathers in removal of heavy metals from wastewater. J Clean Prod 2003; 11: 321–326.

14.

Jin

. Duck feather/nonwoven composite fabrics for removing metals present in textile dyeing effluents. J Eng Fiber Fabr 2013; 3: 21–28.

15.

Moore

GRP

Martellia

Gandolfo

. Influence of the glycerol concentration on some physical properties of feather keratin films. Food Hydrocol 2006; 20: 975–982.

16.

Wang

Liu

. Solution and application of the keratin. Wool Text J 2011; 8: 59–63.

17.

Kar

Misra

. Use of keratin fiber for separation of heavy metals from water. J Chem Technol Biotechnol 2004; 79: 1313–1319.

18.

Aguayo-Villarreal

Bonilla-Petriciolet

Hernández-Montoya

. Batch and column studies of Zn²⁺ removal from aqueous solution using chicken feathers as sorbents. Chem Eng J 2011; 167: 67–76.

19.

Gou

Yang

Meng

. Extraction of wool keratin. Wool Spinning Technol 2011; 3: 18–21.

20.

Sun

Liu

. Chemically modified chicken feather as sorbent for removing toxic chromium(VI) ions. Ind Eng Chem Res 2009; 48: 6882–6889.

21.

Martínez-Hernández

Velasco-Santos

De Icaza

. Microstructural characterization of keratin fibres from chicken feathers. Int J Environ Pollut 2005; 23: 162–178.

22.

Wang

. Study on sizing properties of phthalic acid ester of starch. J Zhongyuan Univ Technol 2010; 21: 52–54.

23.

Wang

Shao

. Investigation of the structure of silk fibroin fiber made by electrospinning process from silk fibroin aqueous solution. J Appl Polym Sci 2006; 101: 961–968.

24.

Tarawou

Wankasi

Horsfall

Jr . Sorption of Manganese(II) and Chromium (III) ions from aqueous solution using water Hyacinth biomass (Eichhorniacrassipes). J Environ Sci Eng 2010; 4: 38–43.

25.

Sun

Zhang

Dong

. The application and mechanism study of sodium sulfide in bulk copper–lead flotation. Nonferrous Met 2011; 2: 52–56.

26.

Zhao

Yue

. The regeneration characteristics of various red mud granular adsorbents (RMGA) for phosphate removal using different desorption reagents. J Hazard Mater 2010; 182: 309–316.

27.

Wang H, Ding XF, Jin XY, et al. A kind of composite meltblown filter cartridge filled with feather fibers—a new method. Patent application 201210019962.2, China, 2012.

28.

Motsa

Thwala

Msagati

TAM

. The potential of melt-mixed polypropylene–zeolite blends in the removal of heavy metals from aqueous media. Phys Chem Earth 2011; 36: 1178–1188.

Adsorption and desorption properties of modified feather and feather/polypropylene melt-blown filter cartridge of lead ion (Pb 2+ )

Abstract

Keywords

Introduction

Experimental

Materials

Modification of the feather fiber

Preparation of feather/PP melt-blown filter cartridges

Adsorption experiment of the feather fiber

Dynamic Pb2+ adsorption measurement of filter cartridges

Desorption experiment

Measurement

ICP-AES

Scanning electronic microscopy (SEM)

Fourier transform infrared (FTIR) spectroscopy analysis

Results and discussion

Influences of Na2S2O5 treatment on Pb2+ adsorption of the feather fiber

Structural changes of the feather fiber before and after Na2S2O5 modification

Desorption effects of Na2S·9H2O and NaOH solutions on the feather fiber

Dynamic Pb2+adsorption properties of feather/PP melt-blown filter cartridges

Conclusion

Footnotes

Declaration of Conflicting Interests

Funding

References

Dynamic Pb²⁺ adsorption measurement of filter cartridges

Influences of Na₂S₂O₅ treatment on Pb²⁺ adsorption of the feather fiber

Structural changes of the feather fiber before and after Na₂S₂O₅ modification

Desorption effects of Na₂S·9H₂O and NaOH solutions on the feather fiber

Dynamic Pb²⁺adsorption properties of feather/PP melt-blown filter cartridges