Sterilization techniques for biodegradable scaffolds in tissue engineering applications

Abstract

Biodegradable scaffolds have been extensively studied due to their wide applications in biomaterials and tissue engineering. However, infections associated with in vivo use of these scaffolds by different microbiological contaminants remain to be a significant challenge. This review focuses on different sterilization techniques including heat, chemical, irradiation, and other novel sterilization techniques for various biodegradable scaffolds. Comparisons of these techniques, including their sterilization mechanisms, post-sterilization effects, and sterilization efficiencies, are discussed.

Keywords

Biodegradable scaffolds tissue engineering sterilization biomaterials

Introduction

Tissue engineering is a growing field that attempts to provide solutions for regeneration of tissues that have been damaged due to diseases or injuries. In order to achieve this, tissue engineering scaffold is commonly used to promote repair and regeneration of tissues. The scaffold, a three-dimensional construct, is designed to support cell infiltration, growth, differentiation, and enhance new tissue development and guide new tissue formation.¹ Many biomaterials have been used to prepare the scaffold, including metals, ceramics, glasses, and polymers.² Recently, there is a growing trend in the use of biodegradable polymers for the fabrication of scaffolds and other implants for various tissue engineering applications. In addition to their well-established biocompatibilities in vivo, biodegradable polymers are preferred for two main reasons: (1) scaffolds fabricated from these materials provide desirable mechanical strength which, in combination with controlled degradation rates, leads to gradual reduction in mechanical strength during tissue regeneration, and (2) complete degradation of the scaffold structure over time eliminates the need for a secondary surgery for the retrieval of the implant, thus allowing faster recovery at the site of injury.

Sterilization is a process by which a product can be made free of contamination from living microorganisms, including bacteria, yeasts, and viruses.³ When sterilizing biodegradable scaffolds, the chosen sterilization technique must maintain structural and biochemical properties of the scaffolds, thereby ensuring that the scaffolds will fulfill their intended purposes post-sterilization. This requirement renders the sterilization of biodegradable scaffold a formidable task.⁴ Most standard sterilization techniques used in the clinical settings, such as ethylene oxide (EtO) and gamma irradiation, have also been used to sterilize biodegradable scaffolds over the last several decades, but these attempts have been largely unsuccessful.⁵ This is because that biodegradable scaffolds are more sensitive, due to the nature of their chemical properties, to the conditions required by these standard sterilization methods. While some emerging sterilization techniques have shown reasonable performances, specific drawbacks associated with these procedures still exist. In this review, we first discuss the mechanisms of these sterilization techniques for microorganism inactivation and subsequently focus on comparing sterilization efficiencies and post-sterilization effects of these sterilization techniques for different biodegradable scaffolds.

Sterilization mechanisms and post-sterilization effects

A biodegradable scaffold has a potential to be infected by a wide range of microorganism, such as virus, bacteria, and fungi. These microorganisms can cause serious infections and diseases, including tetanus, influenza, yellow fever, AIDS, candidiasis, and histoplasmosis.^6,7 Different microorganisms possess different characteristics, and as a result, their resistance levels to sterilization or disinfection techniques differ from each other. In terms of their resistance to sterilizations, in the order from high to low, bacterial spores have been proven to be the most resistant followed by mycobacteria, nonenveloped virus, fungi, bacteria, and enveloped virus.

Various sterilization techniques have been attempted on biodegradable scaffolds. Due to the lack of techniques designed specifically for such scaffolds, conventional sterilization techniques previously established for clinical applications, such as heat treatment, EtO, irradiation, and plasma become the initial choice. Other sterilization techniques that have previously been used only for disinfection purposes such as iodine, peracetic acid (PAA), and some recently developed sterilization techniques such as freeze-drying and supercritical carbon dioxide (sCO₂) are now being experimented for the sterilization of biodegradable scaffolds. Based on the ability to kill different types of microorganism, the inactivation level (commonly defined as high, medium, and low) of these sterilization techniques and their ability in inactivation of certain types of microorganism are summarized in Table 1.⁸ Besides incomplete microorganism inactivation, toxic residues and changes in scaffold structural and biochemical properties can be problematic to the safety and efficacy of scaffolds for studies in vivo. Detailed operation conditions of each method are summarized in Table 2; the advantages, residue effects, penetration abilities of each technique, and their post-sterilization effects on structural and biochemical properties of biodegradable scaffolds are summarized in Tables 3 and 4.

Table 1.

Microorganism inactivation ability of different sterilization techniques.

Category	Technique	Inactivation level	Mycobacteria	Vegetative bacteria	Bacteria spores	Nonenveloped virus	Enveloped virus	Prions	Fungal
Heat	Heat treatment	High	✓	✓	✓	✓	✓	✓	✓
Irradiation	Gamma	High	✓	✓	✓	✓	✓		✓
	E-beam	High	✓	✓	✓	✓	✓		✓
	UV	Medium		✓			✓
Plasma	Plasma	High	✓	✓	✓	✓	✓	✓	✓
Chemical sterilization	EtO	High	✓	✓	✓	✓	✓	✓	✓
	Peracetic acid	High		✓	✓	✓	✓	✓	✓
	Ethanol	Medium	✓	✓			✓		✓
	Iodine	Medium		✓	✓	✓	✓	✓	✓
Novel techniques	sCO₂			✓	✓	✓	✓
	Antibiotics	Low		✓
	Freeze-drying

UV: ultraviolet; EtO: ethylene oxide; sCO₂: supercritical carbon dioxide.

Table 2.

Operation conditions of different sterilization techniques.

Category	Technique	Temperature (°C)	Pressure (MPa)	Concentration	pH	Contact time	Other comments
Heat	Steam	125–130	0.2–0.3			10–30 min	Pre-heating to the desired sterilization temperature
Heat	Dry heat	160				120 min	Pre-heating to the desired sterilization temperature
Irradiation	Gamma					Hours	Dosage, 10–30 kGy
	E-beam					Minutes	Dosage, 25–150 kGy
	UV					2 h	Wavelength (200–280 nm)
Plasma	Plasma	25–70	Varies			0.5–1 h	Gas composition
Chemical sterilization	EtO	30–65	0.1–0.5	400–1200 mg/L		3–6 h	Relative humidity (40%–80%)
	PAA	20–60		800–3000 mg/L	Acidic	Minutes to hours	Relative humidity (20%–80%)
	Ethanol			60%–80%		Minutes⁹
	Iodine	10–40¹⁰		0.1%–1%	3–9¹⁰	Minutes¹¹
Novel techniques	sCO₂	30–60	7.38–20.5		Acidic	0.5–4 h
	Antibiotics					Hours¹²
	Freeze-drying	−50 to 80				Hours¹³

UV: ultraviolet; EtO: ethylene oxide; PAA: peracetic acid; sCO₂: supercritical carbon dioxide.

Table 3.

Summary of effects of sterilization methods on biodegradable scaffolds.

Category	Technique	Condition	Scaffold	Effect of sterilization of scaffold	Result of sterilization method	Reference
Heat	Heat treatment	Steam treatment with air removal, 129°C	PLA	Increase in mechanical strength; decrease in molecular weight	Not tested	Rozema et al.¹⁴
		Dry heat treatment, 135°C, vacuum atmosphere	Lactide copolymers	Increase in molecular weight; decrease in bending strength	Not tested	Gogolewski and Mainil-Varlet¹⁵
Irradiation	Gamma	Dose rate: 2.11 kGy/h	Copolymers of LLA, CL, and DXO	Decrease in molecular weight; random chain scission; cross-linking	Not tested	Plikk et al.¹⁶
		Dosage: 25 kGy, vacuum atmosphere, 140°C, 12 h	Hydroxyapatite–collagen composite scaffolds	Decrease in compressive mechanical strength; increase in degradation rate	Not tested	Yunoki et al.¹⁷
		Dosage: 30.8 kGy	PCL	Increase in the yield point and the maximum stress; alteration in mechanical structure	Not tested	Cottam et al.¹⁸
		Dosage: 25 kGy	Poly[(butylene terephthalate)-co-poly(butylenesuccinate)-block-poly(ethylene glycol)]	Decrease in elongation at break, tensile strength, and molecular weight	Slow cell growth	Wang et al.¹⁹
		Dosage: 39 kGy	PLLA	Decrease in molecular weight and mechanical strength; increase in degradation rate	Not tested	Hooper et al.²⁰
		Dosage: 10–50 kGy, atmosphere	PCL-hydroxyapatite composites	Chain scission	Not tested	Di Foggia et al.²¹
		Dosage: 3 kGy	PLGA	Decrease in tensile strength	Remained sterile for >3 months	Selim et al.²²
	E-beam	Dosage: 25–150 kGy, room temperature	PCL	Cross-linking, chain scission; increase in the modulus of elasticity	Not tested	Olah et al.²³
		Dosage: 26.6 ± 2.0 kGy	Poly(l,dl-lactide) (PLDLLA)	Decrease in inherent viscosity; faster mechanical degradation	Not tested	Smit et al.²⁴
		Dosage: 25–75 kGy, 2.5°C	Copolymers of LLA, CL, and DXO	Decrease in molecular weight; random chain scission	Not tested	Plikk et al.¹⁶
		Dosage: 25 kGy, an inert atmosphere	Poly(LLA-co-DXO)	Decrease in molecular weight	Not tested	Dånmark et al.²⁵
	UV	5–24 h	Me.PEG-PLA	Increase in degradation rate; chain depletion; change to biochemical properties	Not tested	Fischbach et al.⁴
		2 h	Me.PEG-PLA	NA	Not tested	Fischbach et al.⁴
		12 h, 245–365 nm	PLA	Decrease in molecular weight; increase in degradation rate	Effective in inactivating microorganisms	Janorkar et al.²⁶
		30 min–8 h, 254 nm	PLGA and P(LLA-CL)	Decrease in molecular weight, tensile strength; increase in degradation rate; morphological change	Not tested	Dong et al.²⁷
		0.5–2 h, 254 nm	PLGA	Decrease in molecular weight	Generated sterile scaffolds	Braghirolli et al.¹²
Plasma	Plasma	Inert argon gas, 2–10 min for 33 W; 2–40 min for 100 W	PLGA	Affect chemical structure; change degradation behavior; increase in molecular weight	Not tested	Holy et al.²⁸
		Oxygen, carbon dioxide, ammonia plasmas	Polyurethane	Decrease in molecular weight; increase in mechanical property	Not effective	Gorna and Gogolewski²⁹
		Hydrogen peroxide	Polyurethane	Decrease in molecular weight and tensile strength; increase in degradation rate	Activation of microorganism	Gorna and Gogolewski²⁹
		Hydrogen peroxide, 1 h and 39 min, 43°C	PLLA biomaterial	Physical aging; increase in melting and glass transition temperatures, crystallinity, and brittleness	Not tested	Peniston and Choi³⁰
		Hydrogen peroxide, 55 min, 45°C–55°C	Polyurethane	Increase in degradation rate	Not tested	Bertoldi et al.³¹
Chemical treatment	EtO		Poly(DTE carbonate)	Decrease in yield strength and stiffness	Not tested	Hooper et al.²⁰
			Poly(DTO carbonate)	Increase in degradation rate; decrease in molecular weight	Not tested	Hooper et al.²⁰
		100% ethylene oxide atmosphere, 57°C, 2 h	PLGA	Shrinkage in dimensions; decrease in molecular weight; affects brittleness and stiffness	Not tested	Holy et al.²⁸
		18–96 h, 32°C–45°C, 45%–70% humidity	PLDLLA	Delays degradation	Not tested	Smit et al.²⁴
	Peracetic acid	2 h, room temperature	Collagen fibers	Affect structural integrity and bioactive properties	Not tested	Hodde et al.³²
		0.1% PAA, 15 min–24 h	PLGA	Increase in surface roughness and pore size; surface cracking	Not tested	Shearer et al.³³
		0.1% PAA, 3 h, room temperature	PLGA	Decrease in tensile strength and fiber diameter	Remained sterile for >3 months	Selim et al.²²
	Ethanol	70% Ethanol	Chitosan membranes	Increase in tensile strength	Not tested	Marreco et al.³⁴
		70% Ethanol, 15 min–24 h	PLGA	Structural change; decrease in breaking stress and porosity; increase in fragility and surface wrinkling	Not tested	Shearer et al.³³
		70% Ethanol, 5 min, 4°C	PLGA	Decrease in tensile strength and fiber diameter	Became infected within 2–14 days	Selim et al.²²
		70% Ethanol, 0.5–2 h	PLGA	Changes in the morphology and scaffold dimensions; hampering cellular adhesion	Generated sterile scaffolds	Braghirolli et al.¹²
	Iodine	0.1% Iodine solution, 1–12 min	Allografts (pericardial tissue)		Complete inactivation of a wide variety of bacterial organisms	Moore et al.¹¹
Novel techniques	sCO₂	205 bar, 0.6–4 h, 25°C–40°C	PLGA and PLA		Complete inactivation of a wide variety of bacterial organisms	Dillow et al.³⁵
		27.6 MPa, 60 min, 40°C	Hydrogel, poly(acrylic acid-co-acrylamide) potassium salt		Effective in inactivating microorganisms	Jimenez et al.³⁶
		3.3% water, 0.1% hydrogen peroxide, 80 atm, 30 min, 50°C	NA		6-log inactivation of Bacillus pumilus	Checinska et al.³⁷
		0.25% water, 0.15% hydrogen peroxide, and 0.5% acetic anhydride	Collagen-based scaffolds	Increase in compressive modulus	Vegetative bacteria, fungi, and bacteriophages; bacteria spores were inactivated	Bernhardt et al.³⁸
	Antibiotics	Combined with UV irradiation	Polyphosphate; polyphosphonate	NA	Not tested	Richards et al.³⁹
		1% Antibiotic antimycotic solution, 6–31 h, 4°C	PLGA	Increase in roughness	Not tested	Shearer et al.³³
		1% Antibiotic solution, 1–2 h	PLGA	Changes in the morphology and scaffold dimensions	Generated sterile scaffolds	Braghirolli et al.¹²
	Freeze-drying	Combined with gas plasma, 24–72 h	Collagen sponges	NA	Effective in inactivating microorganisms	Markowicz et al.¹³

PLA: poly(lactic acid); LLA: l-lactic acid; CL: ε-caprolactone; DXO: 1,5-dioxepane-2-one; PCL: poly(ε-caprolactone); PLLA: poly(l-lactic acid); PLGA: poly(lactide-co-glycolide); P(LLA-CL): poly(l-lactide-co-ε-caprolactone); UV: ultraviolet; Me.PEG-PLA: poly(d,l-lactic acid)-poly(ethylene glycol)-monomethyl ether diblock copolymer; DTE: desaminotyrosyl-tyrosine ethyl ester; DTO: desaminotyrosyl-tyrosine octyl ester; PAA: peracetic acid; NA: not applicable.

Table 4.

Advantages and disadvantages of sterilization techniques.

Method	Method	Advantages	Disadvantages
Heat	Heat treatment	Simple, fast, effective, high penetration ability, no toxic residues	High temperature, affect the structural properties of biodegradable polymers
Irradiation	Gamma	High penetration ability, low temperature, effective, easy to control, no residue	Induce structural properties changes, dose rate is lower than electron beams, long time
	E-beam	Low temperature, easy to control, no residue, fast	Induce structural properties changes, electron accelerator needed, low penetration ability
	UV	Fast, low temperature, low cost, no toxic residues	Not effective, induce structural and biochemical properties changes of biodegradable polymers under long exposure duration
Plasma	Plasma	Low temperature, improved cell interaction, increasing wettability on surface of biodegradable polymers, fast	May cause changes in chemical and mechanical properties of polymers, leave reactive species
Chemical treatment	EtO	Effective, low temperature	Induce structural property change, leave toxic residue, flammable, explosive, carcinogenic
	Peracetic acid	Low temperature, effective	Structural and biochemical properties change, residual acidic environment
	Ethanol	Low temperature, low cost, no complex equipment, no toxic residue, fast	Not effective, structural and biochemical property change of scaffolds
	Iodine	Low temperature, no structural property change, fast	Affect biochemical property
Novel techniques	sCO₂	No toxic residue, no biochemical property change	May affect porosity and morphology of scaffolds
	Antibiotics	Convenient, simple	Harmful residue, not effective
	Freeze-drying	Low temperature, no structure property change, no toxic residue	Not effective, may affect the biochemical properties of scaffold

UV: ultraviolet; EtO: ethylene oxide; sCO₂: supercritical carbon dioxide.

Heat treatment

There are two most extensively used heat treatments for sterilization: steam sterilization and dry heat sterilization. They are realized by treating the product with either saturated steam at 125°C to 130°C for around 20 min or hot air at 160°C for 2 h, respectively.⁸ The advantage of heat treatment is that it is effective, fast, simple, and without any toxic residues (Table 4).⁴⁰ The penetration ability of heat treatment is one of the best among all of the sterilization techniques,⁴¹ and it can completely eliminate all viable microorganisms (see Table 1). Destruction of essential replication metabolic and structural components of microorganism is lethal during steam heat sterilization, while the killing mechanism of dry heat is mainly due to direct heating and oxidation effects.⁸

However, since most biodegradable polymers have low glass transition temperatures (Tg), the use of heat treatment as a sterilization technique for these scaffolds is problematic (Table 3).⁴² In addition, in the case of steam sterilization, the presence of water vapor has been shown to cause hydrolytic degradation of the material to be sterilized.⁴³ To minimize this side effect, Rozema et al.¹⁴ modified the steam sterilization process for poly(lactic acid) (PLA) scaffolds by introducing cycles consisting of individual phases for air removal, sterilization, and steam removal. However, a substantial loss in molecular weight was still observed, along with an increase in mechanical strength due to recrystallization of the polymer. Similarly, Gogolewski and Mainil-Varlet¹⁵ applied vacuum or inert gas atmosphere in their modified dry heat process in order to reduce operation temperature for PLA sterilization. The researchers observed both increases in PLA molecular weight and decreases in material bending strength. Therefore, when considering heat treatment sterilization approach to sterilize degradable scaffolds, one must be careful about its side effects on material mechanical strength and molecular weight in addition to its possible side effects on the structural properties of the scaffolds due to its high-temperature operation conditions.

Irradiation

In comparison with heat treatments, radiation methods offer features such as low temperatures, short processing time, and comparatively lower cost of operation, making the radiation techniques promising candidates to sterilize biodegradable scaffolds.

Gamma and electron beam irradiation

Gamma (γ) and electron beam (e-beam) irradiation are both categorized as ionizing radiation techniques and are often compared. Gamma irradiation, being electromagnetic in nature, is usually obtained from a source of ⁶⁰Co and is produced within a dose range of 10–30 kGy/h.⁴⁴ In comparison, e-beam irradiation is produced by an accelerating stream of electrons; its dosage depends on the power of the source emitting it. Both treatments work by transferring energy to valence electrons, causing electrons to be ejected from materials to be sterilized through which gamma rays pass. This directly breaks DNA and RNA strands and generates reactive oxygen species (ROS) that damage other important cellular components.^45,46 The ROS have also been shown to cleave phosphodiester backbones of DNA molecules, causing the DNA molecules to degrade.⁴⁵ Gamma and e-beam irradiation have the ability to inactivate both gram-negative and gram-positive bacteria, molds, yeasts, most viruses, and some bacterial spores.⁴⁷ Some endospores are shown to be able to withstand high doses of ionizing irradiation and are not destroyed by it.⁴⁸ Although the reasons for spore resistance to ionizing irradiation are not fully understood, it has been suggested that low core water content plays a role.⁴⁹

While γ radiation sterilization technique is simple, rapid, and effective, it is known to result in changes in scaffold material chemical characteristics, reduced compressive mechanical properties and molecular weights, and increased rates of degradation post-sterilization (see Table 3).^16–18 For example, Cottam et al.¹⁸ studied the effects of γ irradiation on the tensile strength of poly(ε-caprolactone) (PCL). It was found that the yield point was much higher for the irradiated samples than that for the nonirradiated controls. This indicates that γ irradiation considerably altered the mechanical property of the material. Similar effects were reported by Hooper et al.²⁰ who used γ irradiation to sterilize biodegradable scaffolds made from poly(l-lactic acid) (PLLA). The researchers showed that γ irradiated PLLA samples lost most of their mechanical strength and degraded faster than nonsterilized control samples. Furthermore, Yunoki et al.¹⁷ reported that hydroxyapatite–collagen composite scaffolds used in bone tissue engineering experienced reduced compressive mechanical strength and increased rate of degradation after γirradiation.

In comparison, e-beam sterilization is known to cause less degradation to materials as the exposure time of e-beam is usually shorter (see Table 2).⁴¹ For example, in a study to compare the two radiation sterilization techniques, biodegradable scaffolds fabricated from l,l-lactide (LLA), ε-caprolactone (CL), and 1,5-dioxepane-2-one (DXO) copolymers were used. The study showed that more DXO monomers were detected in γ irradiation-treated samples than in e-beam-treated samples, likely due to more pronounced degradation in the case of γ radiation treatment.¹⁶ However, e-beam is also known to have some challenges in its applications. The penetration depth of e-beam is dependent on both the kinetic energy of electrons and the density of the biomaterial being sterilized.⁴⁶ Increasing the intensity of the e-beam irradiation can be damaging to the scaffold structure, whereas decreasing the intensity will limit the penetration depth of the e-beam irradiation, thereby decreasing the effectiveness of the e-beam sterilization.^19,50 As a result, thick scaffolds generally cannot be sterilized by e-beam sterilization technique. Furthermore, as shown in Table 3, e-beam sterilization results vary significantly from materials to materials, depending primarily on chemical bonds and linkages of individual materials.^16,23,44 Therefore, the effect of e-beam sterilization on a specific biomaterial must be thoroughly investigated in pilot studies before this technique can be fully implemented for a particular application. While both radiation sterilization techniques have shortcomings, they are still considered promising candidates for sterilizing degradable scaffolds among all currently available techniques; however, key operating conditions such as radiation dosage and scaffold material moisture must be sufficiently studied in pilot studies and carefully controlled.^22,51

Ultraviolet irradiation

Ultraviolet (UV) irradiation is a new approach to sterilize biodegradable scaffolds. It is often used to sterilize material surfaces and transparent biodegradable scaffolds. UV irradiation results in excitation of electrons and accumulation of photoproducts. This causes damages to DNA molecules and prevents DNA replication, leading to inactivation of microorganisms.⁴⁵ Different microorganisms have different sensitivities to UV irradiations. For example, vegetative bacteria are easily destroyed by UV irradiation, while bacterial spores are more resistant.⁴⁹ In comparison, prions are not sensitive to UV irradiation at all.⁵² Viruses are somewhere in between: some viruses are easily inactivated, whereas others are quite resistant. For instance, naked viruses tend to be more resistant to UV irradiation than enveloped viruses.⁵³ Two parameters have been reported to be important to sterilize biodegradable scaffolds: (1) duration of UV irradiation^4,27 and (2) specific wavelength of UV irradiation²⁶—usually between 200 and 280 nm, although 260 nm is reported to be most lethal.⁴⁸

UV exposure time appears to be one of the most important factors affecting material post-sterilization properties. For example, Fischbach et al.⁴ reported that a short UV radiation exposure of 2 h was able to effectively sterilize poly(d,l-lactic acid)-poly(ethylene glycol)-monomethyl ether diblock copolymer (Me.PEG-PLA) films without causing significant changes to the copolymer, while longer UV exposures between 5 and 24 h caused significant changes on scaffold properties with considerable depletion of PEG chains from the scaffold’s surface.⁴ However, a study by Dong et al.²⁷ found that a shorter exposure time of 1-h UV irradiation caused a drastic reduction in molecular weight and tensile strength for both poly(lactide-co-glycolide) (PLGA) and poly(l-lactide-co-ε-caprolactone) (P(LLA-CL)) nanofiber scaffolds. This discrepancy in the literature seems to suggest that appropriate UV radiation conditions vary for different materials and that they should be carefully studied before fully implemented.

Plasma

Plasma sterilization technique is a method that recently has found applications in sterilization of biodegradable scaffolds. Gas plasma offers many advantages, such as low-temperature operating conditions and improved cell-material interactions likely due to plasma surface modifications.²⁹ Plasma is created by subjecting gas to pulsed discharges of direct current, radio frequency, or microwaves that generates chemically reactive species due to excitation, dissociation, and ionization of electrons. While the mechanism of bacterial inactivation by plasma is still not well understood, it is believed that etching, charged particles, and oxidation from the reactive plasma and radicals are all involved.⁵⁴ Plasma can physically destroy and inactivate spores,⁵⁵ and it is also effective in inactivating bacterial endospores and vegetative bacteria. Although plasma sterilizations would still occur even if the carrier gas on its own has no effect on viable bacteria, most current plasma sterilization protocols include gas mixtures that have bactericidal properties of their own;⁵⁶ generally gas choices are those with high oxygen contents to allow for many ROS to be generated.⁵⁵ The flow rate of gas is also important since it affects the rate at which reactive species are generated. Other important factors include operating pressure, gas temperature, and plasma excitation frequency.⁵⁴

Inert gas plasma sterilization technique is a preferred sterilization technique for biodegradable scaffolds when power and exposure time can be precisely controlled. For example, complete sterility of PLGA scaffold was obtained with the use of high power (100 W) inert argon gas plasma with radio-frequency glow discharge at an exposure time of 4 min. However, a lower power at 33 W and longer exposure time of more than 10 min resulted in significant damage to the three-dimensional structure of the scaffold.²⁸

To improve the microorganism inactivation ability, reactive gas mixtures, especially those with higher oxygen contents, are generally used.⁵⁵ While these reactive gas plasmas are shown to be more effective than inert gases to inactivate highly resistant microorganisms, especially spores,⁵⁴ they are reported to cause material cross-linking or degradation that lead to compromised mechanical properties.^29–31 In addition, the use of reactive gas plasma has been shown to contribute to continued presence of reactive species within the scaffolds even long after sterilization, resulting in potential side effects if the residual reactive species are not properly removed before in vivo studies.^57,58

Chemical sterilization

EtO

EtO is commonly used to sterilize a wide range of medicinal and clinical products, such as rubber and plastic products, due to its low-temperature requirements and extensive range of antimicrobial activity.⁵⁹ EtO causes irreversible alkylation of cellular molecules that may contain amino, carboxyl, thiol, hydroxyl, and amide groups, resulting in permanent suppression of cell metabolism and division.¹⁵ Vegetative gram-negative and gram-positive bacteria, fungal, spores, DNA and RNA viruses, and enveloped and naked viruses are easily inactivated by EtO.⁶⁰ The effectiveness of sterilization by EtO is dependent on operation parameters such as concentration, temperature, duration, and relative humidity (see Table 2).^59,61

As summarized in Table 3, EtO sterilization is known to affect structural and biochemical properties of biodegradable scaffolds. Hooper et al.²⁰ investigated post-sterilization effects of EtO treatment on tyrosine-derived polycarbonates for degradable bone fixation devices and drug delivery applications. The material showed considerable reduction in yield strength and increase in stiffness after sterilization, and the rate of degradation post-sterilization was faster when compared to nonsterilized controls.

Interestingly, EtO sterilization was shown to substantially affect the release pattern of drugs embedded in a biodegradable scaffold. Hsiao et al.⁵⁹ studied the effects of EtO sterilization on the release of vancomycin, an antibiotic, from PLGA scaffold. The study found that EtO-treated scaffolds did not exhibit any burst release during the first 7 days as was seen in the nonsterilized controls. Additionally, the total drug-releasing period for the EtO-treated samples was much shorter than that of an untreated controls, and the overall amount of released antibiotic was also less. Contrasting to this observation, there are other reports showing evidence suggesting that EtO treatments did not alter drug delivery performances post-treatment.^62,63

Residual toxicity of EtO is a major concern for EtO sterilization, especially if small amount of EtO continues to reside inside the scaffold after sterilization. To this end, the American Health Industry Manufacturers Association (HIMA) and the American National Institute for Occupational Safety and Health (NIOSH) have set guidelines of 25–250 ppm as the maximum EtO residual concentration in medical devices post-EtO sterilization, with recommended range of 10–25 ppm.⁶⁴ Given these restrictions, aeration of scaffolds after EtO sterilization is mandatory in order to remove residual EtO. However, one should be cautious about using EtO to sterilize biodegradable polymers, particularly those with low diffusion coefficients as studies have demonstrated that materials that have slow EtO release rates exhibit higher EtO residual concentrations than the allowed 250 ppm upper limit even after 15 days of aeration.⁶⁴

PAA

PAA is a low-temperature sterilization technique with relatively high penetration ability, which can effectively inactivate a wide variety of microorganisms. The production of hydroxyl radicals has been reported to be an important mechanism in bacterial inactivation.⁶⁵ In addition, the oxidizing property of PAA has been shown to cause inactivation of important enzymes in microorganisms.⁴⁵ PAA can effectively inactivate large varieties of microorganisms, including vegetative bacteria, spores, enveloped and naked viruses, and fungi.⁶⁶ Factors that affect PAA antimicrobial activities include PAA concentration, temperature, pH, and relative humidity (see Table 2).⁸ It has been established that the higher the concentration and temperature, the greater the antimicrobial activities.⁸ Furthermore, a synergistic sterilization effect has been reported when PAA is used in combination with hydrogen peroxide.⁶⁷

However, the oxidative and acidic environment created during PAA treatment can cause adverse effects on the biodegradable scaffolds to be sterilized (Table 3).³² For example, Shearer et al.³³ noted increased PLGA scaffold pore sizes and surface roughness after PAA sterilization in their study. In addition, the oxidative PAA process resulted in protein denaturation, thereby significantly limiting its potentials in sterilizing scaffolds loaded with protein-based growth factors for tissue engineering applications. Furthermore, the presence of acidic residuals within the biodegradable scaffold after PAA sterilization raises concerns about the biocompatibilities of the sterilized scaffolds in vivo.^56,66,68

Ethanol

The low cost of treatment and ambient-temperature operating conditions are some of the advantages that ethanol treatment offers.⁶⁹ However, its limited ability to kill microorganisms remains a significant concern. Ethanol causes denaturation of proteins, cellular dehydration, and dissolution of lipids present in cell membranes, resulting in inactivation of certain microorganisms.^34,48 Concentrations of ethanol ranging from 60% to 80% have the ability to inactivate gram-positive, gram-negative, and acid-fast bacteria, as well as lipophilic viruses, while hydrophilic viruses and bacterial spores are known to be resistant to ethanol.⁷⁰

The side effects of ethanol remain controversial in the literature. On one hand, there is documented evidence suggesting that soaking PLGA scaffolds and hollow fibers in 70% ethanol significantly altered their structural and mechanical properties, reduced scaffold porosity, and increased sample surface wrinkling;³³ on the other hand, ethanol sterilization treatment has been shown to have no effect on PLGA scaffold molecular weights and scaffold structures.²⁸

Iodine

Iodine treatment can be carried out at ambient temperature, which makes it an ideal candidate in sterilizing temperature-sensitive biodegradable scaffolds. The exact mechanism of iodine sterilization process on bacterial cells is not well studied. Oxidation, ionization, and membrane immobilization are believed to be possible killing mechanisms.¹⁰ Depending on sterilization parameters, iodine can inactivate vegetative bacteria spores, molds, yeasts, and viruses.¹⁷ Although bacterial spores are resistant to some forms of iodine, it has been shown that when povidone is used as an iodophor for iodine sterilization, some species of spores, such as Bacillus globigii spores, can be significantly reduced (>99%).⁷¹ The efficiency of microbial inactivation decreases significantly with increases in pH.⁴⁵ The concentration of free iodine within the iodine solution has been shown to affect its biocidal effects.⁷²

While there are very few studies reporting the effects of iodine on biodegradable scaffolds, it has been established that 0.1% iodine solution does not affect the structure of allografts for use in implants.¹¹ However, it should be noted that iodine treatment will likely affect biochemical properties of the scaffolds, especially if these scaffolds are loaded with growth factors or viable cells.^73,74 Therefore, further investigation is needed before iodine can be deemed safe to sterilize biodegradable scaffolds, especially those loaded with bioactive ingredients, such as growth factors or cells.

Other novel techniques

sCO₂

The use of sCO₂ as a sterilization technique for biodegradable scaffolds is a relatively new approach. Features such as mild operating conditions, nontoxicity, nonflammability, and low reactivity make sCO₂ an attractive option when compared with other sterilization techniques.^75,76 In addition, zero surface tension allows easy penetration of sCO₂ into complex and porous structures of degradable scaffolds to destroy a host of microorganisms.⁵ While the mechanism of sCO₂ bacterial inactivation process is not completely understood, acidification, lipid modification, inactivation of vital enzymes, and removal of intracellular substances are possible mechanisms;⁷⁷ in particular, acidification has been identified as the most likely cause of inactivation of microorganisms.⁷⁵ Vegetative bacterial cells and certain viruses can be inactivated by sCO₂. For example, Checinska et al.³⁷ achieved inactivation of Bacillus pumilus using sCO₂ with a sterilization process at 100 atm and 50°C that involved three cycles and additional 0.1% hydrogen peroxide. Wayne et al.⁷⁸ established a sCO₂ sterilization protocol with a pressure from 7 to 24 MPa and a temperature from 25°C to 60°C to destroy bacterial spores and sterilize biomedical scaffolds within time periods ranging from 20 min to 12 h. As listed in Table 2, the effectiveness of microbial inactivation by sCO₂ is a function of many parameters, including pressure, temperature, and sCO₂ contact time.³⁵ Sterilization using sCO₂ has been found to be more effective when it is modified with certain compounds, such as acetic acid, tert-butyl hydroperoxide, and hydrogen peroxide.⁷⁹ This is likely due to either acidic or oxidative properties of these modifiers. In addition, some modifiers may also help to improve sCO₂ penetration abilities through cell walls and cytoplasmic membranes, thus enhancing its ability to inactivate microorganisms.⁷⁹

The mild operating conditions at the supercritical state of CO₂ do not cause damage to structural properties of biodegradable scaffolds; the low reactivity of sCO₂ does not cause the formation of radicals and reactive species, thus well maintaining structural properties of biodegradable scaffolds. Dillow et al.³⁵ showed that sterilization with sCO₂ did not cause any changes in the physical and chemical properties of PLGA and PLA. Jimenez et al.³⁶ evaluated the sterilization efficacy of sCO₂ on poly(acrylic acid-co-acrylamide), a model hydrogel biomaterial, and reported that at a pressure of 27.6 MPa and a temperature of 40°C, the hydrogel was effectively sterilized.

Interestingly, sCO₂ method is commonly used to prepare degradable tissue engineering scaffolds.^80–83 For example, Ennett et al.⁸³ incorporated vascular endothelial growth factor (VEGF) and bone morphogenetic protein-2 (BMP-2) into PLA using sCO₂ process and successfully regenerated bone tissue in vivo. Therefore, it would be advantageous to fabricate degradable scaffolds and sterilize these scaffolds simultaneously using sCO₂ in a single step.

Antibiotics

The use of antibiotics as a technique for sterilization of biodegradable scaffolds has not been researched in depth, and there is limited information available in the literature. It is a convenient and simple method. Antibiotics inactivate bacteria by interfering with essential processes such as DNA replication, cell wall synthesis, and protein synthesis. Antibiotic sterilization can be either broad spectrum if they interfere with universal bacterial processes (such as DNA replication) or narrow spectrum if they interfere with processes specific to one group of bacteria.⁸⁴ However, it is only effective against vegetative bacteria and spores while fungi, molds, and viruses are not affected. In addition, bacteria, especially gram-positive bacteria, are rapidly developing resistance to antibiotics.⁸⁴

Antibiotic treatment can be a useful sterilization method if used in combination with other methods or used independently if an effective antibiotic cocktail is employed. For example, it has been shown that UV irradiation followed by antibiotic treatment can be used as an effective sterilization protocol. In addition, antibiotic cocktails are generally used for sterilization applications as different antibiotics act in different ways to inactivate bacterial cells, targeting cell walls and cell membranes, or inactivating essential enzymes in bacteria.⁴⁸ Braghirolli et al.¹² and Shearer et al.³³ reported complete sterilization of PLGA scaffolds using an antibiotic cocktail, which contained penicillin, streptomycin sulfate, and fungizone. However, changes in morphology and dimensions of the PLGA scaffolds were observed. Additionally, antibiotics were shown to leave harmful residual traces in scaffolds after treatment.⁸⁵

Freeze-drying

There are very few studies on the use of freeze-drying (lyophilization) as a sterilization technique for biodegradable scaffolds since its primary use has been preserving tissue transplants.⁸⁶ The microorganism inactivation mechanism of freeze-drying involves the use of low temperature that results in denaturation of proteins and enzymes.⁸⁷ The process of freezing and dehydrating is believed to break intact membrane structures of microorganisms and to remove bound water, resulting in microorganism inactivity.

In general, freeze-drying is a gentle sterilization technique that is not completely efficient and, therefore, has been suggested to be used in combination with other sterilization techniques,⁸⁸ such as γ irradiation⁸⁹ and EtO⁹⁰ in order to improve its overall efficiency to inactivate microorganisms. Markowicz et al.¹³ investigated the effects of freeze-drying combined with gas plasma on collagen sponges. The researchers showed that the combination was effective in inactivating microorganisms. However, more research is needed to establish whether the procedure causes any changes to mechanical and structural properties of the scaffolds. Additionally, proteins have been reported to completely lose their bioactivities due to cold denaturation from freeze-drying process.⁹¹ Therefore, the potential side effect of protein denaturation by freeze-drying should be fully evaluated when this sterilization method is being considered to sterilize degradable scaffolds loaded with bioactive protein-based growth factors.⁹²

Besides the above-mentioned techniques, some other techniques, such as ozone and formaldehyde, have also been evaluated for their potential use to sterilize biodegradable scaffolds. However, their performances in sterilizing biodegradable scaffolds are barely satisfactory. For instance, ozone sterilization has been shown to have detrimental effects on polyurethane (PU) foam in that it significantly altered the PU foam morphology and degradation behavior due to oxidations by ozone.³¹ Similarly, formaldehyde has been shown to affect structures and surface properties of biodegradable polymers. Furthermore, its known toxicity and carcinogenicity also cause major concerns.³⁸

Conclusion

It is a critically important task to choose an appropriate sterilization technique in order to effectively sterilize biodegradable scaffolds but at the same time to maintain their structural and biochemical integrity. Detailed comparisons of commonly used sterilization techniques for biodegradable scaffolds are discussed in this review. It is evident that there is no “perfect” sterilization technique that can achieve excellent sterilization for a wide variety of degradable materials without any adverse post-sterilization effects. As a result, to sterilize biodegradable scaffolds, the operation conditions of a chosen sterilization technique should be precisely controlled and evaluated case by case. In addition, biodegradable scaffolds involve a wide range of materials with different structural and biochemical properties; therefore, different effects might occur with different biodegradable scaffolds with the same sterilization technique. The effectiveness and post-sterilization effects of new emerging techniques need to be further investigated before they can be declared safe and effective for use for biodegradable scaffolds. Finally, with more complex tissue engineering scaffolds being designed and fabricated, combinations of different techniques appear to become the trend to sterilize these tissue engineering devices.

Footnotes

Acknowledgements

The authors acknowledge Angela Melhuish and Grace Zhang for their help with the manuscript.

Declaration of conflicting interest

The author(s) declared no potential conflicts of interest with respect to the research, authorship, and/or publication of this article.

Funding

The author(s) disclosed receipt of the following financial support for the research, authorship, and/or publication of this article: Jennifer Ronholm was supported by Banting and Best Canadian Graduate Scholarship from the Canadian Institutes of Health Research (CIHR), and Yiping Tian was supported by a scholarship from China Scholarship Council (CSC).

References

Hutmacher

Woodfield

TBF

Dalton

. Chapter 10. Scaffold design and fabrication. In: Van Blitterswijk

De Boer

(eds) Tissue engineering. 2nd ed. Oxford: Academic Press, 2014, pp. 311–346.

Nair

Laurencin

. Polymers as biomaterials for tissue engineering and controlled drug delivery. In: Tissue engineering I. Berlin, Heidelberg: Springer, 2005, pp. 47–90.

Gilson

Moon

Hai

. A manual for biomaterials/scaffold fabrication technology. Singapore: World Scientific Publishing Co Pte Ltd, 2007.

Fischbach

Tessmar

Lucke

. Does UV irradiation affect polymer properties relevant to tissue engineering? Surface Science 2001; 491: 333–345.

Zhang

Davis

Matthews

. Sterilization using high-pressure carbon dioxide. J Supercrit Fluid 2006; 38: 354–372.

Cogliati

. Global molecular epidemiology of Cryptococcus neoformans and Cryptococcus gattii: an atlas of the molecular types. Scientifica 2013; 2013: 675213.

Moore

Robson

Trinci

APJ

. 21st century guidebook to fungi with CD. Cambridge: Cambridge University Press, 2011.

McDonnell

Sheard

. A practical guide to decontamination in healthcare. Oxford, UK: John Wiley & Sons, 2012.

Juwarkar

. Cleaning and sterilisation of anaesthetic equipment. Indian J Anaesth 2013; 57: 541.

10.

Block

. Disinfection, sterilization, and preservation. Philadelphia, PA: Lippincott Williams & Wilkins, 2001.

11.

Moore

McIlroy

Phillips

. Nonaldehyde sterilization of biologic tissue for use in implantable medical devices. ASAIO J 1997; 43: 23–30.

12.

Braghirolli

Steffens

Quintiliano

. The effect of sterilization methods on electronspun poly(lactide-co-glycolide) and subsequent adhesion efficiency of mesenchymal stem cells. J Biomed Mater Res B Appl Biomater 2014; 102: 700–708.

13.

Markowicz

Koellensperger

Steffens

GCM

. The impact of vacuum freeze-drying on collagen sponges after gas plasma sterilization. J Biomater Sci Polym Ed 2006; 17: 61–75.

14.

Rozema

Bos

RRM

Boering

. The effects of different steam-sterilization programs on material properties of poly(l-lactide). J Appl Biomater 1991; 2: 23–28.

15.

Gogolewski

Mainil-Varlet

. Effect of thermal treatment on sterility, molecular and mechanical properties of various polylactides. 2. Poly(L/D-lactide) and poly(L/DL-lactide). Biomaterials 1997; 18: 251–255.

16.

Plikk

Odelius

Hakkarainen

. Finalizing the properties of porous scaffolds of aliphatic polyesters through radiation sterilization. Biomaterials 2006; 27: 5335–5347.

17.

Yunoki

Ikoma

Monkawa

. Influence of gamma irradiation on the mechanical strength and in vitro biodegradation of porous hydroxyapatite/collagen composite. J Am Ceram Soc 2006; 89: 2977–2979.

18.

Cottam

Hukins

Lee

. Effect of sterilisation by gamma irradiation on the ability of polycaprolactone (PCL) to act as a scaffold material. Med Eng Phys 2008; 31: 221–226.

19.

Wang

Chen

Liu

. Synthesis and evaluation of biodegradable segmented multiblock poly(ether ester) copolymers for biomaterial applications. Polym Int 2004; 53: 2145–2154.

20.

Hooper

Cox

Kohn

. Comparison of the effect of ethylene oxide and gamma-irradiation on selected tyrosine-derived polycarbonates and poly(L-lactic acid). J Appl Polym Sci 1997; 63: 1499–1510.

21.

Di Foggia

Corda

Plescia

. Effects of sterilisation by high-energy radiation on biomedical poly-(ε-caprolactone)/hydroxyapatite composites. J Mater Sci: Mater M 2010; 21: 1789–1797.

22.

Selim

Bullock

Blackwood

. Developing biodegradable scaffolds for tissue engineering of the urethra. BJU Int 2011; 107: 296–302.

23.

Olah

Filipczak

Czvikovszky

. Changes of porous poly(epsilon-caprolactone) bone grafts resulted from e-beam sterilization process. Radiation Physics and Chemistry 2007; 76: 1430–1434.

24.

Smit

Thomas

Hoogendoorn

RJW

. Sterilization and strength of 70/30 polylactide cages: e-beam versus ethylene oxide. Spine 2007; 32: 742–747.

25.

Dånmark

Finne-Wistrand

Schander

. In vitro and in vivo degradation profile of aliphatic polyesters subjected to electron beam sterilization. Acta Biomater 2011; 7: 2035–2046.

26.

Janorkar

Metters

Hirt

. Degradation of poly(L-lactide) films under ultraviolet-induced photografting and sterilization conditions. J Appl Polym Sci 2007; 106: 1042–1047.

27.

Dong

Yong

Liao

. Degradation of electrospun nanofiber scaffold by short wave length ultraviolet radiation treatment and its potential applications in tissue engineering. Tissue Eng Part A 2008; 14: 1321–1329.

28.

Holy

Cheng

Davies

. Optimizing the sterilization of PLGA scaffolds for use in tissue engineering. Biomaterials 2001; 22: 25–31.

29.

Gorna

Gogolewski

. Molecular stability, mechanical properties, surface characteristics and sterility of biodegradable polyurethanes treated with low-temperature plasma. Polym Degrad Stabil 2003; 79: 475–485.

30.

Peniston

Choi

. Effect of sterilization on the physicochemical properties of molded poly(L-lactic acid). J Biomed Mater Res B: Appl Biomater 2007; 80: 67–77.

31.

Bertoldi

Farè

Haugen

. Exploiting novel sterilization techniques for porous polyurethane scaffolds. J Mater Sci: Mater M 2015; 26: 1–12.

32.

Hodde

Janis

Ernst

. Effects of sterilization on an extracellular matrix scaffold: part I. Composition and matrix architecture. J Mater Sci: Mater M 2007; 18: 537–543.

33.

Shearer

Ellis

Perera

. Effects of common sterilization methods on the structure and properties of poly(D, L lactic-co-glycolic acid) scaffolds. Tissue Eng 2006; 12: 2717–2727.

34.

Marreco

da Luz Moreira

Genari

. Effects of different sterilization methods on the morphology, mechanical properties, and cytotoxicity of chitosan membranes used as wound dressings. J Biomed Mater Res B Appl Biomater 2004; 71: 268–277.

35.

Dillow

Dehghani

Hrkach

. Bacterial inactivation by using near- and supercritical carbon dioxide. Proc Natl Acad Sci USA 1999; 96: 10344–10348.

36.

Jimenez

Zhang

Matthews

. Evaluation of CO2-based cold sterilization of a model hydrogel. Biotechnol Bioeng 2008; 101: 1344–1352.

37.

Checinska

Fruth

Green

. Sterilization of biological pathogens using supercritical fluid carbon dioxide containing water and hydrogen peroxide. J Microbiol Methods 2011; 87: 70–75.

38.

Bernhardt

Wehrl

Paul

. Improved sterilization of sensitive biomaterials with supercritical carbon dioxide at low temperature. PLoS One 2015; 10: e0129205.

39.

Richards

Dahiyat

Arm

. Evaluation of polyphosphates and polyphosphonates as degradable biomaterials. J Biomed Mater Res 1991; 25: 1151–1167.

40.

Ratner

. Biomaterials science: an introduction to materials in medicine. 2nd ed. Oxford, UK: Academic press, 2004.

41.

Silindir

Ozer

. Sterilization methods and the comparison of E-Beam sterilization with gamma radiation sterilization. FABAD J Pharm Sci 2009; 34: 43–53.

42.

Gogolewski

Mainil-Varlet

. The effect of thermal treatment on sterility, molecular and mechanical properties of various polylactides: I. Poly (L-lactide). Biomaterials 1996; 17: 523–528.

43.

Hai

Gilson

Jin

. Polymeric biomaterials. In: Park

Bronzino

(eds) Biomaterials: principles and applications. Roca Raton, FL: CRC Press LLC, 2003.

44.

Leonard

Buchanan

Farrar

. Investigation into depth dependence of effect of E-beam radiation on mechanical and degradation properties of polylactide. Plast Rubber Compos 2006; 35: 303–309.

45.

Fraise

Lambert

Maillard

J-Y

. Russell, Hugo and Ayliffe’s principles and practice of disinfection, preservation and sterilization. 4th ed. Malden, MA: Blackwell Publishing, 2004.

46.

Cox

Battista

. Deinococcus radiodurans—the consummate survivor. Nat Rev Microbiol 2005; 3: 882–892.

47.

Spoto

MHF

Gallo

Alcarde

. Gamma irradiation in the control of pathogenic bacteria in refrigerated ground chicken meat. Sci Agric 2000; 57: 389–394.

48.

Prescott

Harley

Klein

. Microbiology. 6th ed. New York, NY: McGraw-Hill Science/Engineering/Math, 2004.

49.

Setlow

. Spores of Bacillus subtilis: their resistance to and killing by radiation, heat and chemicals. J Appl Microbiol 2006; 101: 514–525.

50.

Aidulis

Pegg

Hunt

. Processing of ovine cardiac valve allografts: 1. Effects of preservation method on structure and mechanical properties. Cell Tissue Bank 2002; 3: 79–89.

51.

Hutmacher

Hürzeler

Schliephake

. A review of material properties of biodegradable and bioresorbable polymers and devices for GTR and GBR applications. Int J Oral Max Impl 1995; 11: 667–678.

52.

Dean

Feldschreiber

Lett

. Repair of X-ray damage to the deoxyribonucleic acid in micrococcus radiodurans. Nature 1966; 209: 49–52.

53.

Watanabe

Miyata

Sato

. Inactivation of laboratory animal RNA-viruses by physicochemical treatment. Jikken Dobutsu 1989; 38: 305–311.

54.

Vicoveanu

Popescu

Ohtsu

. Competing inactivation agents for bacterial spores in radio-frequency oxygen plasmas. Plasma Process Polym 2008; 5: 350–358.

55.

Lerouge

Wertheimer

Yahia

. Plasma sterilization: a review of parameters, mechanisms, and limitations. Plasmas Polym 2001; 6: 175–188.

56.

Laroussi

. Low temperature plasma-based sterilization: overview and state-of-the-art. Plasma Process Polym 2005; 2: 391–400.

57.

Lee

Kim

. Effects of low temperature hydrogen peroxide gas on sterilization and cytocompatibility of porous poly(D,L-lactic-co-glycolic acid) scaffolds. Surf Coat Tech 2008; 202: 5762–5767.

58.

Chau

Kao

Blank

. Microwave plasmas for low-temperature dry sterilization. Biomaterials 1996; 17: 1273–1277.

59.

Hsiao

C-Y

Liu

S-J

Ueng

SW-N

. The influence of gamma irradiation and ethylene oxide treatment on the release characteristics of biodegradable poly(lactide-co-glycolide) composites. Polym Degrad Stabil 2012; 97: 715–720.

60.

Moore

Gendler

. Viruses adsorbed on musculoskeletal allografts are inactivated by terminal ethylene oxide disinfection. J Orthop Res 2004; 22: 1358–1361.

61.

Lerouge

Simmons

. Sterilisation of biomaterials and medical devices. Oxford, UK: Elsevier, 2012.

62.

Thakur

Florek

Kohn

. Electrospun nanofibrous polymeric scaffold with targeted drug release profiles for potential application as wound dressing. Int J Pharm 2008; 364: 87–93.

63.

Dormer

Gupta

Scurto

. Effect of different sintering methods on bioactivity and release of proteins from PLGA microspheres. Materials Science and Eng C Mater Biol Appl 2013; 33: 4343–4351.

64.

Vink

Pleijsier

. Aeration of ethylene oxide-sterilized polymers. Biomaterials 1986; 7: 225–230.

65.

Clapp

Davies

French

. The bactericidal action of peroxides; an E.P.R. spin-trapping study. Free Radic Res 1994; 21: 147–167.

66.

Lomas

Cruse-Sawyer

Simpson

. Assessment of the biological properties of human split skin allografts disinfected with peracetic acid and preserved in glycerol. Burns 2003; 29: 515–525.

67.

Alasri

Valverde

Roques

. Sporocidal properties of peracetic acid and hydrogen peroxide, alone and in combination, in comparison with chlorine and formaldehyde for ultrafiltration membrane disinfection. Can J Microbiol 1993; 39: 52–60.

68.

Lapeikova

Lapeik

Smolka

. Application of radio frequency glow discharge plasma for enhancing adhesion bonds in polymer/polymer joints. J Appl Polym Sci 2006; 102: 1827–1833.

69.

Huebsch

Gilbert

Healy

. Analysis of sterilization protocols for peptide-modified hydrogels. J Biomed Mater Res Part B 2005; 74B: 440–447.

70.

Ali

Dolan

Fendler

. Alcohols. Philadelphia: Lippincott Williams & Wilkins, 2001.

71.

Mosley

Gills

Krushefski

. Evaluating the formulae for integrated lethality in ethylene oxide sterilization using six different endospore forming strains of bacteria, and comparisons of integrated lethality for ethylene oxide and steam systems. PDA J Pharm Sci Technol 2005; 59: 64–86.

72.

Stanford

Solomon

Levick

. Sterilization of contaminated bone-tendon autografts using 10% povidone-iodine solution. Orthopedics 1999; 22: 601–604.

73.

Gottardi

. Iodine and iodine compounds. Philadelphia: Lea and Febiger, 1991.

74.

Severyns

Lejeune

Rocoux

. Nontoxic antiseptic irrigation with chlorhexidine in experimental revascularization in the rat. J Hosp Infect 1991; 17: 197–206.

75.

White

Burns

Christensen

. Effective terminal sterilization using supercritical carbon dioxide. J Biotechnol 2006; 123: 504–515.

76.

Alvi

Kang

. Effects of sterilization on implant mechanical property and biocompatibility. Int J Artif Organs 2005; 28: 1126–1137.

77.

Spilimbergo

Bertucco

. Non-thermal bacteria inactivation with dense CO₂. Biotechnol Bioeng 2003; 84: 627–638.

78.

Wayne

Carrol

Lydia

. Sterilization methods and apparatus which employ additive-containing supercritical carbon dioxide sterilant. Patent US 7108832, 2005.

79.

Shieh

Paszcyznski

Wai

. Sterilization of Bacillus pumilus spores using supercritical fluid carbon dioxide containing various modifier solutions. J Microbiol Methods 2009; 76: 247–252.

80.

Ginty

Howard

Upton

. A supercritical CO₂ injection system for the production of polymer/mammalian cell composites. J Supercrit Fluid 2008; 43: 535–541.

81.

Duarte

ARC

Mano

Reis

. Preparation of chitosan scaffolds loaded with dexamethasone for tissue engineering applications using supercritical fluid technology. Eur Polym J 2009; 45: 141–148.

82.

Zhu

Lee

Jackson

JSH

. Characterization of porous poly (D, L-lactic-co-glycolic acid) sponges fabricated by supercritical CO2 gas-foaming method as a scaffold for three-dimensional growth of Hep3B cells. Biotechnol Bioeng 2008; 100: 998–1009.

83.

Ennett

Kaigler

Mooney

. Temporally regulated delivery of VEGF in vitro and in vivo. J Biomed Mater Res A 2006; 79: 176.

84.

Hancock

. Mechanisms of action of newer antibiotics for Gram-positive pathogens. Lancet Infect Dis 2005; 5: 209–218.

85.

Leeming

Lovering

Hunt

. Residual antibiotics in allograft heart valve tissue samples following antibiotic disinfection. J Hosp Infect 2005; 60: 231–234.

86.

Smith

Young

Kearney

. Mechanical properties of tendons: changes with sterilization and preservation. J Biomech Eng 1996; 118: 56–61.

87.

Privalov

. Cold denaturation of proteins. Crit Rev Biochem Mol Biol 1990; 25: 281–305.

88.

Uhlenhaut

Dorner

Pauli

. Effects of lyophilization on the infectivity of enveloped and non-enveloped viruses in bone tissue. Biomaterials 2005; 26: 6558–6564.

89.

Cornu

Banse

Docquier

. Effect of freeze-drying and gamma irradiation on the mechanical properties of human cancellous bone. J Orthop Res 2000; 18: 426–431.

90.

Bechtold

Eastlund

Butts

. The effects of freeze-drying and ethylene-oxide sterilization on the mechanical-properties of human patellar tendon. Am J Sports Med 1994; 22: 562–566.

91.

Chen

. Formulation concerns of protein drugs. Drug Dev Ind Pharm 1992; 18: 1311–1354.

92.

Abdul-Fattah

Kalcinia

Pikal

. The challenge of drying method selection for protein pharmaceuticals: product quality implications. J Pharm Sci 2007; 96: 1886–1916.

Sterilization techniques for biodegradable scaffolds in tissue engineering applications

Abstract

Keywords

Introduction

Sterilization mechanisms and post-sterilization effects

Heat treatment

Irradiation

Gamma and electron beam irradiation

Ultraviolet irradiation

Plasma

Chemical sterilization

EtO

PAA

Ethanol

Iodine

Other novel techniques

sCO2

Antibiotics

Freeze-drying

Conclusion

Footnotes

Acknowledgements

Declaration of conflicting interest

Funding

References

sCO₂