Friction stir welding of titanium alloy (Ti–6Al–4V) was demonstrated on 3, 6, 9 and 12 mm thickness square groove butt joints. Complete microstructural and microhardness evaluations were conducted in addition to surface and subsurface examinations for each case. The 3 mm welds exhibited an extremely fine grained microstructure with evidence of processing temperatures below the beta transus temperature of the alloy. The 6, 9 and 12 mm samples possessed larger grains formed by a slower cooling rate from above the beta transus temperatures. The thick section weld exhibited a nearly uniform microhardness, while the thinner welds showed a slight, 6%, increase in hardness compared with the parent material.
WelschG., BoyerR. and CollingsE. W. (eds.): ‘Materials properties handbook: titanium alloys’; 1994, Materials Park, OH, ASM International.
2.
MishraR. S. and MahoneyM. W. (eds.): ‘Friction stir welding and processing’; 2007, Materials Park, OH, ASM International.
3.
MishraR. S. and MaZ. Y.: Mater. Sci. Eng. R, 2005, R50, 1–78.
4.
NandanR., DebRoyT. and BhadeshiaH. K. D. H.: Prog. Mater. Sci., 2008, 53, 980–1023.
5.
TrappT., HelderE. and SubramanianP. R.: in ‘Friction stir welding and processing II’, 173–178; 2003, San Diego, CA, TMS.
6.
JataK. V., SubramanianP. R., ReynoldsA. P., TrappT. and HelderE.: Proc. Int. Offshore and Polar Engineering Conf., Toulon, France, May 2004, ISOPE, 22–27.
7.
LeeW. B., LeeC. Y., ChangW. S., YeonY. M. and JungS. B.: Mater. Lett., 2005, 59, (26), 3315–3318.
8.
ShangY., SatoY. S., KokawaH., ParkS. H. C. and HiranoS.: Mater. Sci. Eng. A, 2008, A488, 25–30.
9.
ZhangY., SatoY. S., KokawaH., ParkS. H. C. and HiranoS.: Mater. Sci. Eng. A, 2008, A485, 448–455.
10.
LienertT. J.: in ‘Friction stir welding and processing’, Chapter 7, 123–154; 2007, Materials Park, OH, ASM International.
11.
SandersD., RamuluM., Klock-McCookE., EdwardsP., ReynoldsA. and TrappT.: J. Mater. Eng. Perform., 2008, 17, (2), 187–192.
12.
SandersD., RamuluM. and EdwardsP.: Materialwiss. Werkstofftech., 2008, 39, (4–5), 353–357.
13.
RamirezA. J. and JuhasM. C.: Mater. Sci. Forum, 2003, 426–432, 2999–3004.
14.
Klock-McCookE. J.: ‘Characterization of friction stir welded and superplasticly formed friction stir welded joints of titanium’, Master thesis, University of Washington, Seattle, WA, USA, 2005.
15.
EdwardsP. D.: ‘Experimental and numerical characterization of friction stir welded and superplastically formed – friction stir welded titanium’, Master thesis, University of Washington, Seattle, WA, USA, 2006.
16.
JohnR., JataK. V. and SadanandaK.: Int. J. Fatigue, 2003, 25, (9–11), 939–948.