A simple series of test was developed to highlight and compare the difference between the static strain induced transformation (SSIT) and the dynamic strain induced transformation (DSIT) mechanism in grain refinement and also to investigate the origin of the difference between the two mechanisms. The results showed that while the SSIT sets up a two-dimensional impingement among the ferrite grains, it cannot avoid their coarsening (normal growth). However, the DSIT forms a group of grains with a three-dimensional impingement which does not coarsen and maintains their fine size throughout the transformation, thereby, reduces the final average grain size.
TamuraI.: Proc. Int. Conf. on ‘Physical metallurgy of thermo-mechanical processing of steels and other metals’, Tokyo, Japan, 1988, The iron and Steel Institute of Japan,1–10.
2.
TanakaT.: Int. Met. Rev., 1981, 26, 185–209.
3.
HodgsonP. D., HicksonM. R. and GibbsR. K.: Mater. Sci. Forum, 1998, 284-286, 63–72.
4.
RiosP. R., deI.. BottS., SantosD. B., de. MeloT. M. F. and FerreiraJ. L.: Mater. Sci. Technol., 2007, 23, 417–422.
5.
BaeY. H., HongS. H., SeoD. H., ChoiJ. K. and ChooW. Y.: Proc. Conf. on ‘Ultrafine grained materials II’, 635-642; 2002, TMS.
6.
ChoiJ. K., SeoD. H., LeeJ. S., UmK. K. and ChooW. Y.: ISIJ Int., 2003, 43, 746–754.
7.
PriestnerR. and HodgsonP. D.: Mater. Sci Technol, 1992,8, 849–854.
8.
BengocheaR., LopezB. and GutierrezI.: Metall. Mater. Trans. A, 1998, 29A, 417–426.
9.
HurleyP. J., MuddleB. C. and HodgsonP. D.: Metall. Mater. Trans. A, 2002, 33A, 2985–2993.
10.
BeladiH., KellyG. L. and HodgsonP. D.: Int. Mater. Rev., 2007, 52, 14–28.
11.
HodgsonP. D., CollinsD. C. and PerretB.: Proc. 7th Int. Symp. on ‘Physical simulation’, Japan, 1997, Dynamic Systems Inc. & NRIM Japan, 219.
12.
PandiR. and YueS.: ISIJ Int., 1993, 34, 270–279.
13.
KirkaldyJ. S. and BaganisE. A.: Metall. Mater. Trans. A, 1978, 9A, 495–501.
14.
OuchiC., SampeiT. and KozasuI.: Trans. ISIJ, 1982, 22, 214–222.
15.
PriestnerR. and RiosE. DE. I.: Met. Technol., 1980, 7, 309–315.