Polymers for Use in Controlled Release Systems: The Effect of Surfactants on their Swelling Properties

Abstract

The effect of an ampholytic surfactant on the swelling properties of polymeric materials was studied, using various swelling liquids. Tablets were prepared consisting of hydroxypropyl methylcellulose, poly(oxyethylene) and sodium alginate. Tego betain was the non-ionic surfactant used as an additive in a series of samples made of the above polymers. Those tablets were immersed in distilled water, phosphate buffer and 0.1 N HCl, and their weight uptake was recorded as a function of time, in order to assess the swelling process. Measurements of the contact angle of the above systems were also carried out for estimating their wetting properties.

The results of this study showed a selectivity among polymers, surfactant and surrounding liquid. Clearly, an enhancement of the swelling capacity of hydroxypropyl methylcellulose tablets due to the surfactant was recorded. An unclear effect was observed in the case of poly(oxyethylene), whereas for sodium alginate, the dominant factor is its water solubility that controls swelling behaviour.

Keywords

controlled release surfactant swelling polymeric drugcarriers

References

1. Wada, R. , S.H. Hyon and Y. Ikada . 1990. Lactic acid oligomer microspheres containing hydrophilic drugs, J. Pharm. Sci., 79:919-924.

2. Avgoustakis, K. and J.R. Nixon . 1991. Biodegradable controlled release tablets, 1: Preparative variables affecting the properties of poly(lactide-co-glycolide), Intern. J. Pharm., 70:77-85.

3. Andreopoulos, A.G. 1995. Controlled release of newer quinolone from biodegradable systems based on poly(lactic acid), J. Biomater. Appl., 10:163-168.

4. Nitsch, M.J. and U.V. Banakar . 1994. Implantable Drug Delivery., J. Biomater. Appl., 8:247-284.

5. Shih, C. , T. Higuchi and K. J. Himmelstein . 1984. Drug delivery from catalyzed erodible polymeric matrices of poly(ortho esters), Biomaterials, 5:237.

6. Lee, P.I. 1983. Dimensional changes during release from glassy hydrogel matrix, Polym. Commun., 24:45.

7. Hopfenberg, H. and K. Hsu . 1978. Swelling-controlled, constant rate delivery systems, Polym Eng. Sci. 18:1186.

8. Dounis, E. , T. Korakis , A. Anastasiadis , K. Kanellakopoulou , A. Andreopoulos and H. Giamarellou . 1996. Sustained release of fleroxacin in vitro from lactic acid polymer, Bulletin Hosp. for Joint Diseases, 55:17.

9. Andreopoulos, A.G. , T. Korakis , E. Dounis , K. Kanellakopoulou , A. Anastasiadis and P. Tzivelekis . 1996. In vitro release of new quinolones from biodegradable systems. A comparative study., J. Biomater. Apple, 10:338.

10.

10. Andreopoulos, A.G. , E.C. Hatzi and M. Doxastakis . 1999. Synthesis and Properties of Poly(lactic acid), J. Mater. Sci., Mater. in Med., 10:29.

11.

11. Andreopoulos, A.G. , 1989. Preparation and swelling of polymeric hydrogels, J. Appl. Polym. Sci., 37:2121.

12.

12. Andreopoulos, A.G. 1989. Properties of poly (2-hydroxyethyl acrylate) hydrogels, Biomaterials, 10:101.

13.

13. Vlachou, M. , N.H. Choulis , M. Efentakis and A.G. Andreopoulos . 1996. The effect of modification of acrylic resins on controlled release and bioadhesion, J. Biomater. Appl., 10:217.

14.

14. Buckton, G. , A. Kee and M. Efentakis . 1996. The interaction between hydroxypropylmethylcellulose and sodium dodecyl sulfate, J. Pharm. Sci., 2:1-2.

15.

15. Efentakis, M. , E.C. Hatzi and A.G. Andreopoulos . 1998. Development, evaluation and release characteristics in vitro of oral mucosal bioadhesive matrices containing tetracycline for application to the oral cavity, S.T.P. Pharma Sciences, 8:227.

16.

16. Vlachou, M. et al. "Swelling properties of various polymers used in controlled release systems," paper submitted for publication in J. Biomater. Appl.