Kinetics Analysis of Thermal Degradation Reaction of PVA and PVA/Starch Blends

Abstract

The kinetics of thermal degradation of PVA and PVA/starch (40/60) blends were investigated by thermogravimetry (TGA) and derivative thermogravimetry (DTG). Experiments under non-isothermal conditions were carried out for samples in nitrogen at heating rates of 5, 10, 15 and 20°C/min. The Kissinger, Flynn—Wall—Ozawa, and Coats—Redfern methods were used to calculate the activation energy of degradation and determine the degradation mechanism for PVA and PVA/starch blends. The results showed that these three methods were suitable and effective to describe the thermal degradation of PVA and PVA/starch blends. The thermal stability of PVA/ starch blends is higher than that of PVA suggesting that the addition of starch improved the thermal stability of PVA. The thermal degradation of the PVA/starch blends could be separated into three distinct stages. The Coats—Redfern method showed that the degradation mechanism of PVA and PVA/starch blends was a nucleation and growth mechanism in which PVA went to the A₃ mechanism and PVA/starch blends went to the A₄ mechanism.

Keywords

PVA PVA/starch blends thermal degradation kinetics analysis.

References

Tudorachi, N. , Cascaval, C.N. , Rusu, M. and Pruteanu, M. (2000). Testing of Polyvinyl Alcohol and Starch Mixtures as Biodegradable Polymeric Materials, Polym. Test., 19(7): 785-799.

Yun, Y.H. , Na, Y.H. and Yoon, S.D. (2006). Mechanical Properties with the Functional Group of Additives for Starch/PVA Blend Film, J. Polym. Environ., 14(1): 71-78.

Bastioli, C. , Bellotti, V. , Giudice , L.D. and Gilli, G. (1993). Mater-Bi: Properties and Biodegradability, J. Environ. Polym. Degrad., 1: 181-191.

Pavol, A. , Darina, K. , Miroslav, K. , Dusan, B. and Barbora, S. ( 2002). Poly(vinyl alcohol) Stabilisation in Thermoplastic Processing, Polym. Degrad. Stab., 78(3): 413-421.

Sreedhar, B. , Sairam, M. , Chattopadhyay , D.K. , Syamala Rathnam , P.A. and Mohan Rao, D.V. ( 2005). Thermal, Mechanical, and Surface Characterization of Starch-Poly(vinyl alcohol) Blends and Borax-Crosslinked Films, J. Appl. Polym. Sci., 96: 1313-1322.

Sreedhar, B. , Chattopadhyay , D.K. , Sri Hari Karunakar, M. and Sastry, A.R.K. ( 2006). Thermal and Surface Characterization of Plasticized Starch Polyvinyl Alcohol Blends Crosslinked with Epichlorohydrin, J. Appl. Polym. Sci. , 101: 25-34.

Kissinger, H.E. (1975). Reaction Kinetic in Diffemtial Thermal Analysis, Anal. Chem., 29: 1702-1706.

Popescu, C. ( 1996). Integral Method to Analyze the Kinetics of Heterogeneous Reactions Under Non-Isothermal Conditions: a Variant on the Ozawa-Flynn-Wall Method, Thermochim. Acta, 285(2): 309-323.

Dowdy, D.R. ( 1987). Meaningful Activation Energies for Complex Systems-I. The Application of the Ozawa-Flynn-Wall Method to Multiple Reactions, J. Therm. Anal., 32(1): 137-147.

10.

Coats, A.W. and Redfern, J.P. (1964). Kinetic Parameters from the Thermogravimetric Data, Nature, 201: 68-69.

11.

Tomaszewicz, E. and Kotfica, M. (2004). Mechanism and Kinetics of Thermal Decomposition of Nickel(II) Sulfate(VI) Hexahydrate , J. Therm. Anal. Calorim., 77(1): 25-31.

12.

Sun, J.T. , Huang, Y.D. , Gong, G.F. and Cao , H.L. (2006). Thermal Degradation Kinetics of Poly(methylphenylsiloxane) Containing Methacryloyl Groups, Polym . Degrad. Stab., 91(2): 339-346.