Experimental and theoretical methods for optimal solids loading calculation in MIM feedstocks fabricated from powders with different particle characteristics

Abstract

The aim of this work is to investigate the influence of the particle characteristics of powder to the mixing stage of the powder injection moulding process to identify the best procedure with which to evaluate the optimal solids loading for feedstock fabrication. To perform the present study, powder blends that are made from three bronze and four Inconel 718 powders, with different particle size distributions and morphologies, are mixed with a binder system that is based on polyethylene and wax. Powder–binder blends are prepared by varying the powder content to study how the powder characteristics affect the optimal solids loading. In addition, a new method is presented for determining the optimal solids loading in powder injection moulding feedstocks through the activation energy calculation of powder–binder blends that are prepared with different powder contents. This novel method is compared with the optimal loading values that have been determined by other ways as torque rheometry, determination of the tap-real density ratio and through rheological models.

Keywords

PIM MIXING TORQUE RHEOMETRY OPTIMAL SOLIDS LOADING ACTIVATION ENERGY

References

German

R. M

: ‘Injection molding of metals and ceramics’, Met. Powder Indust. Feder., 1997.

Janardhana Reddy

, Vijayakumar

, Mohan

T. R. R.

and Ramakrishnan

: J. Eur. Ceram. Soc., 1996, 16, 567–574.

Markhoff

C. J.

, Mutsuddy

B. C.

and Lennon

J. W.

: Adv. Ceram., 1984, 9, 246–250.

Warren

and German

R. M.

: ‘The effect of powder characteristics on binder incorporation for injection molding feedstock’, in ‘Compendium on metal injection molding II’; 1989, Princeton, NJ, Metal Powder Industries Federation.

Eilers: ‘The viscosity of emulsions made of highly viscous’, Kolloid Z., 1941, 97, 313–321.

Mooney: ‘The viscosity of a concentrated suspensions of spherical particles’, J. Colloid Set e, 1951, 6, 162–170.

Chong

J. S.

, Christiansen

E. B.

and Baer

A. D.

: ‘Rheology of concentrated suspensions’, J. Appl. Polymer Set, 1971, 15, 2007–2021.

Maron

S. H.

and Pierce

P. E.

: ‘Application o free-eyring general-izad for theory to suspensions of spherical particles’, J. Colloid Set, 1956, 11, 80–95.

Janardhana

. Reddy, N. Ravi and M. Vijayakumar: ‘A simple model for viscosity of powder injection moulding mixes with binder content above powder critical binder volume concentration’, J. Eur. Ceram. Soc., 2000, 20, 2183–2190.

10.

Herranz Sanchez-Cosgalla

: ‘Desarrollo de nuevas formulaciones de ligantes basadas en polietileno de alta densidad para el procesado de aceros rápidos tipo M2 mediante moldeo por inyección de metales’, Thesis, Carlos III University of Madrid, Leganés, Spain, 2004.

11.

Rodriguez Senin

: ‘Desarrollo del proceso de moldeo por inyección de polvos para la obtención de ferritas blandas utilizando sistemas ligantes termoplásticos y termoestables’, Thesis, Carlos III University of Madrid, Leganés, Spain, 2007.

12.

Agote

, Odriozola

, Gutiérrez

and Soares

: aheological study of waste porcelain feedstocks for injection moulding’, J. Eur. Ceram. Soc., 2001, 21, 2843–2853.

13.

Contreras

J. M.

, Jiménez-Morales

and Torralba

J. M.

: aheological behaviour of MIM feedstocks fabricated from powders with different morphologies and particle size distribu-tions’, J. Powder Technol, submitted.

14.

‘Determination of apparent density of free-flowing metal powders using the hall apparatus’, MPIF 04:1985, Metal Powder Industries Federation, 1985.

15.

Dihoru

L. V.

, Smith

L. N.

and German

R. M.

: ‘Experimental analysis and neural network modelling of the rheological behaviour of powder injection moulding feedstocks formed with bimodal powder mixtures’, Powder Metall., 2000, 43, (1), 31–36.

16.

‘Determination of tap density of metal powders’, MPIF 46:1986, Metal Powder Industries Federation, 1986.

17.

Raman

and German

R. M.

: ‘Mixing of injection molding feedstock using batch and continuous mixers’, in ‘Advances in powder metallurgy and particulate materials’, Vol. 4, 1–14; 1994, Princeton, NJ, Metal Powder Industries Federation.

18.

Barreiros

F. M.

and Vierira

M. T.

: TIM of non-conventional particles’, Ceram. Int., 2006, 32, (3), 297–302.

19.

Takekawa

: ‘Injection molding of stainless steel powders’, J. Jpn Soc. Powder Powder Metal I, 1988, 35, (7), 641–645.

20.

Kaully

, Siegmann

and Shacham

: ‘Rheology of highly filled natural CaCO3 composites. I. Effects of solids loading and particle size distribution on capillary rheometry’, Polym. Compos., 2007, 28, 512–523.

21.

Honek

, Hausnerova

and Saha

: ‘Relative viscosity models and their application to capillary flow data of highly filled hard-metal carbide powder compounds’, Polym. Compos., 2005, 26, 30–36.

22.

Huang

, Liang

and Qu

: ‘The rheology of metal injection molding’, J. Mater. Process. Technot, 2003, 137, 132–137.

23.

Takahashi

, Hayashi

and Suzuki

: ‘Improvement of the rheological properties of the zircona/polypropylene system for ceramic injection moulding using coupling agents’, J. Mater. Set, 1992, 27, 5297–5302.

24.

Karatas

, Kocer

, Unal

H. I.

and Saritas

: aheological properties of feedstocks prepared with steatite powder and polyethylene-based thermoplastic binders’, J. Mater. Process. Technot, 2004, 152, (1), 77–83.